- Polymer Property : Tear Strength = 175 pli
Polymer Property : Tear Strength = 175 pli Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tear Strength | 30.7 kN/m | 175 pli | post cured- 2 hours at 177°C; Die B |
| Multibase SILASTIC® Q7-4720 Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase |
|||
| Tear Strength | 30.6 kN/m | 175 pli | Die C, 510 mm/min; ASTM D624 |
| PolyOne Geon™ Vinyl Flexible B6000 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tear Strength | 30.6 kN/m | 175 pli | Die C, 510 mm/min; ASTM D624 |
| PolyOne Geon™ Vinyl Flexible R5145B Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tear Strength | 30.6 kN/m | 175 pli | Die C, 510 mm/min; ASTM D624 |
| PolyOne Geon™ Vinyl Flexible R5145A Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Warp/Longitudinal direction |
| Saint-Gobain Chemlam® RL® RL1000 PTFE-Coated Polyester/Cotton Blend Reinforced Laminate Description: The CHEMLAM® series features unique combinations of multi-layer fluoropolymer films laminated to a variety of reinforcement fabrics. The RL product line features a film of fully sint.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Warp/Longitudinal direction |
| Saint-Gobain Chemlam® RL® RL7000 PTFE-Coated Polyester/Cotton Blend Reinforced Laminate Description: The CHEMLAM® series features unique combinations of multi-layer fluoropolymer films laminated to a variety of reinforcement fabrics. The RL product line features a film of fully sint.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Initial Tear Strength |
| Saint-Gobain CHR® 280-6(R) Roll Covering Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Initial Tear Strength |
| Saint-Gobain CHR® 2915-10 Glass Cloth Backing Silicone Adhesive Pressure Sensitive Tape Description: Glass cloth offers excellent abrasion resistance and mechanical properties, as well as high tensile strength and extreme temperature resistance. Service temperatures range from -100°.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Initial Tear Strength |
| Saint-Gobain CHR® SG03-05(R) Premium Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Initial Tear Strength |
| Saint-Gobain CHR® SG05-05(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Initial Tear Strength |
| Saint-Gobain CHR® SG05-06(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Initial Tear Strength |
| Saint-Gobain CHR® SG06-05(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Initial Tear Strength |
| Saint-Gobain CHR® SG56-06(R) Anti-Static Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Warp/Longitudinal direction; ASTM D1000 |
| Saint-Gobain COHRlastic® 3010 Low Temperature Flexibility Silicone Coated Fabric Description: Saint Gobain Performance Plastics CHR standard COHRlastic silicone coated fabrics, available from stock, have silicone rubber dispersion coated on both sides of fiberglass. They are thi.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Tensile Strength (Fill) |
| Saint-Gobain Chemfab® SlipGrip™ 10 PTFE/Silicone Coated Fiberglass Fabric Description: SlipGrip™ products are PTFE-coated fiberglass fabrics with silicone rubber on one face. This unique combination provides a "slippery" PTFE surface and a "grippy" silicone surface. .. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Tensile Strength (Fill) |
| Saint-Gobain Chemfab® 10 Tear Resistant PTFE-Coated Glass Description: Chemfab® Tear Resistant Series is manufactured with specialized coating materials to improve tear and crease resistance. Uses for this series includes release sheets, belting and gas.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Tensile Strength (Fill) |
| Saint-Gobain Chemfab® 11 Premium PTFE-Coated Glass Description: Chemfab® Premium Series combines a superior quality glass fabric with a high level of PTFE content. Description: Chemfab® Premium is an excellent multi-purpose fabric with a smoot.. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Tensile Strength (Fill) |
| Saint-Gobain Chemfab® 13 Anti-Static PTFE-Coated Glass Description: Chemfab® Anti-static Series is a high quality PTFE-coated glass fabric that can be used for release sheets, belting, or other applications requiring the dissipation of static electri.. |
|||
| Tear Strength | 30.6 kN/m | 175 pli | Die C |
| TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Laminar Filler MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st.. |
|||
| Tear Strength | 30.6 kN/m | 175 pli | ISO 34 |
| DuPont Vamac® GXF Sample Compound Vulcanizate Slab Cure (5 minutes at 190°C) Without Armeen® 18D Test slab is cured for 5 minutes at 190°C and post cured for 4hrs at 175°C. Vulcanizate performance test data can help end-users evaluate the potential fitness of similar compounds for their own .. |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Die C; ASTM D 624 |
| CPT C-Flex® R70-082 Clear Biocompatible TPE C-Flex® is a family of patented thermoplastic elastomers which range in hardness from 5 shore A to 95 shore A. C-Flex® TPE's are biocompatible polymer blends which meet or exceed the current.. |
|||
| Tear Strength | 30.6 kN/m | 175 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 180°C |
| Dow Nordel® IP 4770P Heat Resistant Peroxide Compound FormulationNordel® IP 4770P |
|||
| Tear Strength | 30.6 kN/m | 175 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 180°C |
| Dow Nordel® IP 4770R Heat Resistant Peroxide Compound FormulationNordel® IP 4770R |
|||
| Tear Strength | 30.7 kN/m | 175 pli | Tensile Strength (Fill) |
| Saint-Gobain Chemfab® 10 Porous PTFE-Coated Glass Description: Chemfab® Porous Series products are lightweight, highly porous materials commonly used as a release (non-stick) layer for composite curing, molding, and other processes that "off-gas.".. |
|||