Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.41 - 199 GPa | 930 - 28900 ksi | Average value: 75.9 GPa Grade Count:30 |
Overview of materials for Epoxy/Carbon Fiber Composite This property data is a summary of similar materials in the MatWeb database for the category "Epoxy/Carbon Fiber Composite". Each property range of values reported is minimum and maximum values of a.. |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | |
Epoxy Novolac 27%, Carbon fabric 73% Epoxy Novolac - Dow Chemical "DEN 438". Carbon fabric - "VCA" |
|||
Flexural Modulus | 6.41 GPa @Temperature 175 °C |
930 ksi @Temperature 347 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA), 65% GlassMineral (Dry) Amodel® AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifica.. |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF004 PES LNP THERMOCOMP* JF004 is a compound based on Polyethersulfone resin containing 20% Glass Fiber. |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Asia Pacific) LNP* THERMOCOMP* JF004 is a compound based on Polyethersulfone resin containing Glass Fiber. |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MX85738 PP (Asia Pacific) LNP* Thermocomp* MX85738 is a compound based on Polypropylene resin containing Glass Fiber. |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS LNP THERMOCOMP* ZF004 is a compound based on PPE+PS resin containing 20% Glass Fiber. |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MX85738 PP LNP* THERMOCOMP* MX85738 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | Tangent; ASTM D790 |
Plastics Group Polifil® GFABS-30 30% Glass-Reinforced Acrylonitrile-Butadiene Styrene (ABS) Polifil® GFABS series compounds combine the most desirable properties of both components - allowing for enhanced processability and toughness together with the stiffness of glass.Applications: Fire.. |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | ASTM D790 |
Ecomass® 1080ZB92 Filled Polyamide Nontoxic alternative to Lead (Pb), radiation shielding applications.Moderate Specific GravityFilled Polyamide (PA) alloyExcellent ToughnessInformation provided by Technical Polymers |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | ASTM D790 |
Ensinger XP-154 Compression Molded PI Compound, 40% Graphite, Premium Grade The XP 150 Series are amorphous high performance polyimides with high permanent temperature and creep resistance, as well as excellent bearing and wear properties, and excellent long term thermal st.. |
|||
Flexural Modulus | 6.41 GPa | 930 ksi | ASTM D790 |
Aaron Industries AAROPRENE® GFABS 4030 Glass Filled Acrylonitrile-Butadiene Styrene AAROPRENE® GFABS 4000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
Flexural Modulus | 6.41 GPa @Temperature 175 °C |
930 ksi @Temperature 347 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically .. |