Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.85 GPa | 558 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers OPTRENE 30GF Polypropylene, 30% Glass Reinforced Properties of chemically coupled glass reinforced (30%) polypropylene with high strength and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All .. |
|||
Flexural Modulus | 3.85 GPa | 558 ksi | 2 mm/min; ISO 178 |
Inno-Comp INNOPOL® CS 1-3260 55% Chalk-Filled Polypropylene Homopolymer INNOPOL® CS 1-3260 is a 55% chalk-filled polypropylene homopolymer compound /PP-H KD55 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 1-3260 is developed f.. |
|||
Flexural Modulus | 3.85 GPa | 558 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10 LNP* LUBRICOMP* QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant. |
|||
Flexural Modulus | 3.85 GPa | 558 ksi | ISO 178 |
Solvay TECHNYL® A 216 S30 PA66, 30% glass spheres, DRY Description: Polyamide 66, reinforced with 30% of glass spheres, for injection molding.Available in: EuropeProduct Applications: TECHNYL® A 216 S30 is used in all sectors of industry, offering an.. |
|||
Flexural Modulus | 3.85 GPa | 558 ksi | ISO 178-93 |
Wellman EcoLon® MRGF1619-BK3 19% Mineral/Glass Reinforced Post Consumer Compound Nylon 66 Description: Mineral/Glass Reinforced Post Consumer Compound Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 3.85 GPa | 558 ksi | ISO 178 |
Wellman Wellamid® MR259 22LH-N 25% Mineral Reinforced Nylon 66, Lubricated & Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co.. |
|||
Flexural Modulus | 3.85 GPa | 558 ksi | ISO 178 |
DSM Fibre Intermediates Nyrim® 1525 (Glass), Dry Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is processed via Reaction Injection Moulding (RIM) tec.. |
|||
Flexural Modulus | 3.85 GPa | 558 ksi | STN EN ISO 178 |
Plastcom SLOVAMID 6 T 30 Polyamide 6, 30% Micronized Talc FeaturesDecreased shrinkage against the BT types, increased heat application up to 170°C. Increased tensile modulus - strength of the material. PA matrix reduction. Application for tools, fillin.. |
|||
Flexural Modulus | 3.85 GPa | 558 ksi | ISO 178 |
Solvay TECHNYL® A 218 S30 Black 21 N PA66, 30% glass fiber, DRY Description: Polyamide PA66, reinforced with 30% of glass spheres, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL® A 218 S30 is used in all sectors of indu.. |