Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.300 GPa | 43.5 ksi | ISO 178 |
Polimeri Europa Flexirene® MS 40 U Linear Low Density Polyethylene Flexirene MS 40 U is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 40 U are characterized by a good balance be.. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | ISO 178 |
Polimeri Europa Flexirene® MS 40 A Linear Low Density Polyethylene Flexirene MS 40 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 40 A are characterized by a good balance be.. |
|||
Flexural Modulus | 0.300 GPa @Temperature 90.0 °C |
43.5 ksi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilamid A3 H ZE High Impact PA66 Description: Nilamid A3 H ZE was developed for applications which are subjected to very high shock loads, also at minus temperatures. It has good impact performance, whilst maintaining good strength.. |
|||
Flexural Modulus | 0.300 - 0.300 GPa @Temperature 90.0 - 90.0 °C |
43.5 - 43.5 ksi @Temperature 194 - 194 °F |
Average value: 0.300 GPa Grade Count:1 |
Overview of materials for Nylon 66, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Impact Grade". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP HX00059 PA11 (Europe-Africa-Middle East) LNP * Lubricomp * HX00059 is a compound based on PA 11 resin, containing a Proprietary Lubricant. Added features include: Internally Lubricated. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | |
Shandong Guangyin Special Resin for Badminton Features and Applications: Wear resistance, higher strength, better tenacity, strong adhesion and better low temperature resistance. It is applicable to surface coating of wires, cables, optical cab.. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | |
SPS Guang Zhou POPTREEâ„¢ 6001 Flame-retarded Polyethylene Characteristic: Low density, superior melt flow index, high notched impact strengthApplications: X'mas decorative productInformation Provided by SPS (Guang Zhou) Ltd. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | ISO 178 |
Chengdu Polyster H7560 Thermoplastic Polyether-ester Elastomer (TPEE) High modulus molding and injection grade. Contains improved color- stable antioxidants. Good balance of modulus and toughness. Parts and components of automobile, wires, cables and optical fiber, ho.. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | ISO 178 |
Chengdu Polyster H7560Y Thermoplastic Polyether-ester Elastomer (TPEE) High modulus molding and extrusion grade. Contains improved color- stable antioxidants. Low frictional coefficient and good abrasion resistance. Spherical socket of ball joint and lock of automobile.. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | ISO 178 |
Eurostar Starpylen HU 70E3 HDPE, Injection Molding Starpylen HU 70E3 is a High Density Polypropylene Injection Molding Resin (also known as HU70E3)Information provided by Eurostar. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | 2 mm/min; ISO 178 |
Eurostar Starpylen MH0200A HDPE, Injection Molding Starpylen MH0200A is a High Density Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | ASTM D790 |
Aclo Accucomp Polyethylene LD0102L Low Density |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | ASTM D790 |
Aclo Accucomp Polyethylene LD0109L Low Density |
|||
Flexural Modulus | 0.300 GPa | 43.5 ksi | ISO 178 |
Borealis LE6025 Polyethylene Modified Jacketing Compound LE6025 is a black low density copolymer modified polyethylene compound. It is characterized by excellent stress crack resistance and mechanical properties and low temperature performance in combinat.. |