Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | Average value: 1900 MPa Grade Count:18 |
Overview of materials for Polycarbonate, UV Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, UV Stabilized". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 1239 Polycarbonate, Blow Molding/Extrusion Grade
(discontinued **) Pseudoplastic behavior and high viscosity extrusion and injection molding grade, BgVV- and FDA grade for food contact applications, high melt stability, better resistance to hot water, specially sui.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Bayblend® FR 90 N Polycarbonate/ABS Blend Flame retardant grade with antimony, chlorine and bromine free, flame retardant package, optimized processability.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was sepa.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 1804 Polycarbonate MVR (300 °C/1.2 kg) 6.0 cm3/10 minhigh viscosityUV stabilizedoptimized for low plate-outimproved flammabilityUL 94 V-2/1.5 mm and 3.0 mmavailable in transparenttranslucent and opaque colorssolid sh.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2256 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2400 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2405 MAS048 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 2407 Polycarbonate, Injection Grade Very easy flowing injection molding grade with easy mold release and UV stabilizer.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officia.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2556 Polycarbonate MVR (300 °C/1.2 kg) 14 cm3/10 minEasy releaseGood hydrolysis resistanceInjection moldingAvailable in transparentTranslucent and opaque colorsFood contact gradePreprocessingMax. Water content |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2656 Polycarbonate ISO 7391-PC,MR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minFood contact qualityMedium viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAv.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 2658 Polycarbonate, Injection Grade Easy flowing BgVV- and FDA injection molding grade with easy mold release, for food contact applications, better resistance to hot water.Information provided by Bayer.As of 1 September 2015, Bayer M.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2665 MAS071 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2665 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medium viscosity, easy.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2800 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2805 MAS152 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 2806 Polycarbonate ISO 7391-PC,M,(,,)-09-9MVR (300 °C/1.2 kg) 9.5 cm3/10 minFood contact qualityMedium viscosityGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAvailable in transparenttran.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 3105 Polycarbonate Injection molding and extrusion grade with high viscosity, with easy mold release.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and official.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 3107 MAS167 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® 3152 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Food contact quality•.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 3158 Polycarbonate Key Features:Release agentUnfilledSuitable processing methods:Injection moldingExtrusionBlow moldingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 3208 Polycarbonate Injection molding and extrusion grade with high viscosity, BgVV- and FDA grade for food contact applications, yields especially tough parts, better resistance to hot water.Information provided by Ba.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® AL 2643 Polycarbonate, Injection Grade Easy flowing injection molding grade, UV-stabilized.Applications: Automotive lens applications, fulfills U.S. specification SAE J 576C.Information provided by Bayer.As of 1 September 2015, Bayer Mat.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® LQ 2647 Polycarbonate, UV-Stabilized UV-stabilized injection molding grade with easy mold release, suitable for spectacle glasses (LQ = Lens Quality).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separ.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® 1143 Polycarbonate Pseudoplastic behavior and high viscosity extrusion grade with UV stabilizer and easy mold release, special grade for twin-wall sheet.Information provided by Bayer.As of 1 September 2015, Bayer Mate.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® DP1-1843* Polycarbonate ISO 7391-PC,RL,(,,)-09-9Developmental productMVR (300 °C/1.2 kg) 9.5 cm3/10 minMedium viscosityUV stabilizedRotomoldingAvailable in transparent and translucent colorsGlobe lightsAs of 1 September 2.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® ET2613 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• Medium vi.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® ET3127 Polycarbonate Makrolon® polycarbonate resinMain characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characterist.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® ET3227 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• High visc.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | |
Covestro Makrolon® KU 1-1216 Polycarbonate, UV-Stabilized UV-stabilized injection molding grade, good flow, suitable for spectacle glasses (LQ = Lens-Quality).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Ba.. |
|||
Tensile Creep Modulus, 1000 hours | 1900 MPa | 276000 psi | ISO 899-1 |
Covestro Makrolon® LQ2687 Polycarbonate ISO 7391-PC,MLR,(,,)-18-9MVR (300 °C/1.2 kg) 12.5 cm3/10 minOptical lensMedium viscosityUV stabilizedUV 400 cut offEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in clear t.. |