Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | |
Arkema Group Oroglas® HFI-7 Acrylic
(discontinued **) OROGLAS HFI-7 is a medium impact grade that in addition to the improvement in impact resistance provides superior flow which contribute to reduce the cycle time and improve demolding.Key features :.. |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 |
Lanxess Pocan® B 1501 000000 PBT PBT, non-reinforced, injection molding, extrusion, food contact |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 |
Lanxess Pocan® B 1505 000000 PBT PBT, non-reinforced, injection molding, extrusion |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 |
BASF Ultraform® H2320 004 POM Description: Is a POM, high-molecular-weight grade for extrusion of small thin-walled pipes and panel.Information provided by BASF |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 |
BASF Ultraform® N2320 006 POM Description: Is a POM, high-molecular-weight grade with somewhat increased flowability for injection molding of relatively thick-walled moldings.Information provided by BASF |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa @Strain <=0.500 % |
189000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultradur® B 4406 PBT Description: Is a PBT, flame-retardant injection-molding grades, unreinforced for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and lighting compo.. |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa @Strain <=0.500 % |
189000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultraform® S2320 003 POM Description: Easy flowing and rapidly freezing grade for injection molding difficult, thin-walled part.Information provided by BASF |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 |
BASF Ultraform® S2320 003 PRO BK 00120 POM Description: Is a POM, is a standard flowing and rapidly freezing grade suitable for standard functional applications.Information provided by BASF |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa @Strain <=0.500 % |
189000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultradur® B 4300 K4 20% Glass Bead Filled PBT Description: Is a PBT + ASA, Injection-molding grades containing 20% of glass beads for industrial parts with low warpage.Applications: Precision parts for optical instruments, fuel tank sensor unit.. |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa @Strain <=0.500 % |
189000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultradur® B 4300 M2 12.5% Mineral Filled PBT Description: Is a PBT-HI, mineral-reinforced, impact-modified injection-molding grade for rigid parts, for example automotive power door locks.Information provided by BASF |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | |
Arkema Group Oroglas® SG 7 Acrylic, Gamma Radiation Resistant
(discontinued **) OROGLAS SG 7 is special Gamma - radiation - resistant formulation designed for use in medical devises.OROGLAS SG 10 maintains exceptional clarity after 5 megarads of Gamma radiation with no adverse .. |
|||
Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 |
Lanxess Pocan® B 1600 000000 PBT PBT, non-reinforced, injection molding, extrusion, food contact |