Polymer Property : Tensile Strength, Ultimate = 2610 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	18.0 - 18.0 MPa @Temperature 60.0 - 60.0 °C	2610 - 2610 psi @Temperature 140 - 140 °F	Average value: 18.0 MPa Grade Count:1
Overview of materials for Polystyrene, Heat Resistant Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Heat Resistant Grade". Each property range of values reported is minimum and maximum values..
Tensile Strength, Ultimate	7.00 - 18.0 MPa	1020 - 2610 psi
ATG s.r.l. BR Polybutadiene Rubber
Tensile Strength, Ultimate	9.00 - 18.0 MPa	1310 - 2610 psi
ATG s.r.l. EACM Ethylene-Acrylic Rubber
Tensile Strength, Ultimate	6.00 - 18.0 MPa	870 - 2610 psi
ATG s.r.l. EPDM Ethylene-Propylene Terpolymer
Tensile Strength, Ultimate	6.00 - 18.0 MPa	870 - 2610 psi
ATG s.r.l. EPM Ethylene-Propylene Copolymer
Tensile Strength, Ultimate	7.00 - 18.0 MPa	1020 - 2610 psi
ATG s.r.l. IIR Butyl Rubber
Tensile Strength, Ultimate	9.00 - 18.0 MPa	1310 - 2610 psi	Average value: 11.4 MPa Grade Count:28
Overview of materials for Low Density Polyethylene (LDPE), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Extrusion Grade". Each property range of values reported is minimum and..
Tensile Strength, Ultimate	10.3 - 18.0 MPa	1500 - 2610 psi	Average value: 14.1 MPa Grade Count:23
Overview of materials for Low Density Polyethylene (LDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Blow Molding Grade". Each property range of values reported is minimum ..
Tensile Strength, Ultimate	7.00 - 18.0 MPa @Temperature 60.0 - 120 °C	1020 - 2610 psi @Temperature 140 - 248 °F	Average value: 12.3 MPa Grade Count:1
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are..