Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 55.0 - 76.0 MPa | 7980 - 11000 psi | Average value: 64.3 MPa Grade Count:3 |
Overview of materials for Polyphthalamide (PPA), High Impact This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, High Impact". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Ultimate | 12.4 - 76.0 MPa | 1800 - 11000 psi | Average value: 26.9 MPa Grade Count:206 |
Overview of materials for Polystyrene, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Impact Modified". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Ultimate | 5.50 - 76.0 MPa | 798 - 11000 psi | Average value: 13.1 MPa Grade Count:17 |
Overview of materials for EMAAA Terpolymer This property data is a summary of similar materials in the MatWeb database for the category "EMAAA Terpolymer". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Tensile Strength, Ultimate | 48.0 - 76.0 MPa | 6960 - 11000 psi | Average value: 61.4 MPa Grade Count:5 |
Overview of materials for Polycarbonate/Styrenic Alloy This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Styrenic Alloy". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Ultimate | 32.0 - 75.8 MPa | 4640 - 11000 psi | Average value: 57.6 MPa Grade Count:15 |
Overview of materials for Cyclo Olefin Polymer This property data is a summary of similar materials in the MatWeb database for the category "Cyclo Olefin Polymer". Each property range of values reported is minimum and maximum values of appropria.. |
|||
Tensile Strength, Ultimate | 21.0 - 75.8 MPa | 3050 - 11000 psi | Average value: 56.7 MPa Grade Count:15 |
Overview of materials for Fluorocarbon ETFE, with Glass or Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Fluorocarbon ETFE, with Glass or Carbon Fiber Filler". Each property range of values reported is minimum.. |
|||
Tensile Strength, Ultimate | 25.0 - 75.5 MPa | 3630 - 11000 psi | Average value: 39.2 MPa Grade Count:34 |
Overview of materials for Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded". Each property range of values reported is m.. |
|||
Tensile Strength, Ultimate | 11.0 - 75.8 MPa | 1600 - 11000 psi | Average value: 41.7 MPa Grade Count:25 |
Overview of materials for Polyphenylene Sulfide (PPS) with PTFE Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with PTFE Filler". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 62.1 - 75.8 MPa | 9000 - 11000 psi | |
Bulk Molding Compounds BMC 840 Corrosion Resistant Molding Compound BMC 840 is a very high strength, corrosion resistant compound suitable for compression, transfer and stuffer injection molding.Typical applications are pump housings and impellers. |
|||
Tensile Strength, Ultimate | 53.0 - 76.0 MPa | 7690 - 11000 psi | Average value: 61.7 MPa Grade Count:12 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |