Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 |
Nylene® 9110 Unfilled Nylon 6/10 Description: Nylene® 9110 is an unfilled specialty nylon. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation... |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 |
Nylene® Naxel™ PC1210 Polycarbonate Description: Naxel™ PC1210 is a 6 melt, general purpose polycarbonate. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources.. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 |
Nylene® Naxel™ PC45G FR 10% Glass Reinforced, Flame Retardant Polycarbonate Description: Naxel™ PC45G FR is a 10% glass fiber reinforced, flame retardant polycarbonate. PC45G FR is UL approved. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins ar.. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D412 |
2055D Polyurethane-based Biomedical Elastomer |
|||
Tensile Strength, Ultimate | 62.1 - 152 MPa | 9000 - 22000 psi | Average value: 98.7 MPa Grade Count:27 |
Overview of materials for Polycarbonate/ABS Alloy, NCG Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, NCG Fiber Filled". Each property range of values reported is minimum and maximu.. |
|||
Tensile Strength, Ultimate | 62.05 MPa | 9000 psi | |
Abatron AboCast 8-2/Abocure 8-2 Epoxy
(discontinued **) 2-part solvent-free dielectric epoxy casting compound.Processing: 100/50 ratio (pbw); Gel time, 100 g (3.5 oz.): 265 minutes; cures in 3 weeks at 25°C (77°F).Applications: solventless casting, adh.. |
|||
Tensile Strength, Ultimate | 62.05 MPa | 9000 psi | |
Abatron AboCast 8-13/Abocure 8-13 Epoxy
(discontinued **) 2-part, clear, solvent-free dielectric epoxy casting compound.Processing: 100/12.80 ratio (pbw); Gel time, 100 g (3.5 oz.): 53 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°.. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | |
Hybrid Plastics Nanoreinforced® POSS® Polyimide Nanoreinforced® POSS® Polyimide is a hybrid nanocomposite that can serve as oxidation resistant and highly bondable form of polyimide. Upon exposure to oxidizing oxygen the POSS® polyimide .. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 |
Global PC-1403 Standard Grade Polycarbonate Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 |
Global PC-1424 Standard Grade Polycarbonate Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 |
Global PC-1603 Standard Grade Polycarbonate Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Ultimate | 62 MPa | 9000 psi | ASTM D638 |
Sumitomo Bakelite Durez® 152 Phenolic, Injection Grade Durez 152 Phenolic is a two-stage, heat resistant/electrical molding material. It exhibits superior dimensional stability, good strength retention at elevated temperature and good molded appearance.. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D412 |
Lubrizol Estane® AG 9550 Thermoplastic Polyurethane Type: Estane® AG 9550 is a polyether based aliphatic polyurethane designed for flat die extrusion into film and sheet products.Features: Very tough, high modulus, high tear and tensile properties t.. |
|||
Tensile Strength, Ultimate | 62.1 MPa @Temperature 760 °C |
9000 psi @Temperature 1400 °F |
|
Crucible Steel 416 Plus Chromium Steel Crucible 416 Plus is a hardenable chromium steel to which elements have been added to improve machinability and non-galling characteristics. Better machinability than that of standard AISI Type 4.. |
|||
Tensile Strength, Ultimate | 62.05 MPa | 9000 psi | |
Abatron AboCast/AboCure 8109-2 High melting point. Filled version.Processing: 100/10 pbw; 90 minute potlife; mix at 130-140°C (270 °F); cures in 16 h/120°C (250°F), 10 h/140°C (285°F), 8 h/160°C (320°F), 2 h/ 200°C (390°.. |
|||
Tensile Strength, Ultimate | 62.05 MPa | 9000 psi | |
Abatron AboCast/AboCure 8109-4 Safety hardener (minimum toxicity) version of 8109-3.Processing: 100/10 pbw; Potlife: 2.5 h/20°C (68°F), 30 min/40°C (105°F), 15 min/60°C (140°F); mix at RT; cures in: 24 h/20°C (68°F), 2-3 .. |
|||
Tensile Strength, Ultimate | 62.05 MPa | 9000 psi | |
Abatron AboCast/AboCure 8109-9 Minimum toxicity version of 8109-8.Processing: 100/25 ratio; Potlife: 45 min/20°C (68°F), 20 min/40°C (105°F), 10 min /60°C (140°F); mix at RT; cures in: 24 h/20°C (68°F), 2-3 h/60°C (140°.. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | |
AdvanSource Biomaterials ChronoFlex® AL 65D Biodurable Medical Grade Polyurethane ChronoFlex® AL is a family of premium polycarbonate aliphatic biodurable thermoplastic polyurethane elastomers developed by AdvanSource Biomaterials Corporation. ChronoFlex® AL medical-grade elas.. |
|||
Tensile Strength, Ultimate | 62.1 - 115 MPa | 9000 - 16700 psi | Average value: 96.0 MPa Grade Count:12 |
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc.. |
|||
Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 |
Techmer ES Electrafil® DB-50/SS/6 Polycarbonate, 6% Stainless Steel Fiber (dry blend) |