Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
Shell Carilon® DB6F0A10 Polyketone, Flame-Retarded (V-0) Injection Molding Grade
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6F0A10 is a flame-retarded injection molding grade with mechanical properties which classify it a.. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D412 |
Covestro Texin® 5286 Thermoplastic Polyurethane, Polyether-based, Medical
(discontinued **) This grade is in chemical compliance with 21 CFR 177.1680 (Polyurethane Resins) and 177.2600 (Rubber articles intended for repeated use) subject to the limitations of this regulation and any other r.. |
|||
Tensile Strength, Ultimate | 38.0 - 110 MPa | 5510 - 16000 psi | Average value: 54.5 MPa Grade Count:12 |
Overview of materials for Acetal Copolymer, Silicone Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Silicone Filled". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 38.0 - 85.0 MPa @Temperature 60.0 - 120 °C |
5510 - 12300 psi @Temperature 140 - 248 °F |
Average value: 58.4 MPa Grade Count:3 |
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
Global GM-2860 High Density Polyethylene, Injection Molding Grade
(discontinued **) Description-opacity, medium high stiffness, good impact strength, good chemical resistanceApplications- auto parts, bottles, housewares, drums, containers, bottlesMeets FDA requirements as listed in.. |
|||
Tensile Strength, Ultimate | 38.0 - 120 MPa | 5510 - 17400 psi | Average value: 64.6 MPa Grade Count:17 |
Overview of materials for Phenolic, Novolac, Cellulose Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Cellulose Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Ultimate | 38.0 - 105 MPa | 5510 - 15200 psi | Average value: 70.9 MPa Grade Count:17 |
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ.. |
|||
Tensile Strength, Ultimate | 38.0 - 150 MPa | 5510 - 21800 psi | Average value: 78.2 MPa Grade Count:87 |
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
IDI Composites 44-10 MW Thermoset Polyester, Molding Moderate strength material specifically formulated for microwave oven performance.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | |
Haveg 41NA Phenolic; Silicate Filled A proprietary thermoset plastic consisting of a phenol-formaldehyde resin and non-asbestos silicate fillers. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | DIN 53504 |
Lubrizol ESTANE® 5778 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ISO 527-1 |
Chengdu Polyster CH7563 Thermoplastic Polyether-ester Elastomer (TPEE) Poly-basic block copolymer. Good compatibility with PBT, PET and PA. For blending with PBT, PET and PA to improve impact resilience properties.Information provided by Chengdu Polyster Co., Ltd. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638/D412 |
Covestro Bayflex® 190 Polyurethane Elastomeric RIM, 20% Mica Filled, MDI-based 2-Component Liquid System 0.150 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o.. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638/D412 |
Covestro Bayflex® 190 Polyurethane Elastomeric RIM, 20% Mineral Filled, MDI-based 2-Component Liquid System 0.150 in. thickness. Calcium Silicate filled. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was se.. |
|||
Tensile Strength, Ultimate | 38.0 - 47.0 MPa | 5510 - 6820 psi | |
Arkema Group Rilsan® Fine Powders Natural Polyamide 11 Rilsan® fine powder coatings offer weatherability, long-lasting adhesion, chalk resistance, chemical resistance to aliphatic hydrocarbons, bases, salt solutions, oils, greases and other petroleum p.. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® 0.1 Mos PTFE; Molybdenum Disulfide Filled
(discontinued **) Data provided by the manufacturer.0.1 wt.% Molybdenum Disulfide. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric propert.. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
PolyOne Lubri-Tech™ SF-000/40T Polyphenylene Sulfide - 40% PTFE
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638 |
Sumitomo Bakelite North America FM 3000 Cellulose Reinforced Phenolic Novolac FM 3000 is a self-lubricated cellulose reinforced phenolic molding compound, modified for applications requiring reduced friction and low wear. Information supplied by Sumitomo Bak North America... |
|||
Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 38.0 - 89.3 MPa | 5510 - 13000 psi | Average value: 59.5 MPa Grade Count:125 |
Overview of materials for Acrylic, Optical Grade, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Optical Grade, Molded". Each property range of values reported is minimum and maximum values of.. |