Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 245 MPa @Temperature 980 °C |
35500 psi @Temperature 1800 °F |
|
Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Ultimate | 245 MPa | 35500 psi | 5mm/min; ISO 527 |
BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Dry) Ultramid HMG13 HS BK-102 is a 63% glass filled, injection molding, high modulus nylon designed to have high strength and stiffness for metal replacement applications. It also has excellent moldabil.. |
|||
Tensile Strength, Ultimate | >= 245 MPa | >= 35500 psi | Guaranteed Minimum L-T Direction |
Aleris HOGAL 5558 Aluminum 5026-O/H111 HOGAL 5558 is produced according to EN AW-5026.Information provided by Aleris. |
|||
Tensile Strength, Ultimate | 245 MPa @Temperature 982 °C |
35500 psi @Temperature 1800 °F |
|
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |