Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 10 Rod and Bar; A (TB00) Temper; All Sizes (UNS C17500) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 10 Wire; A (TB00) Temper; 1.3-12.7 mm Diameter (UNS C17500) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | >= 240 MPa | >= 34800 psi | |
Kobe Steel KS40 Commercially Pure Titanium, ASTM Gr. 1, Annealed Nominal Composition: Ti-Fe-OApplications: PHE, press formed parts, roofs, walls Features: Excellent formability, Excellent corrosion resistanceInformation provided by Kobe Steel |
|||
Tensile Strength, Ultimate | >= 240 MPa | >= 34800 psi | |
Kobe Steel KS40PDA Titanium alloy with low alloying elements, ASTM Gr. 11, Annealed Nominal Composition: Ti-0.15 Pd Applications: Condenser tubes, heat transfer tubes, piping, linings, electrolysis vessels, chemical use.Features: Super corrosion resistant. Information provided by .. |
|||
Tensile Strength, Ultimate | >= 240 MPa | >= 34800 psi | |
Kobe Steel KS40S Commercially Pure Titanium, ASTM Gr. 1, Annealed Nominal Composition: Ti-Fe-OApplications: PHE, press formed parts, roofs, walls Features: Excellent formability, Excellent corrosion resistanceInformation provided by Kobe Steel |
|||
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 3 Forgings & Extrusions; A (TB00) Temper (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; A (TB00) Temper; All Thicknesses (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 3 Rod and Bar; A (TB00) Temper; All Sizes (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 3 Wire; A (TB00) Temper; 1.3-12.7 mm Diameter (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | >= 240 MPa | >= 34800 psi | |
MetalTek MTEK 65 UNS C90700 Gear Bronze Copper-tin alloy with high tensile, yield and compressive strength as well as wear resistance.Applications: Worm gears, steel mill nutsInformation provided by MetalTekCast UNS C90700; Cast Grade C90.. |
|||
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 10 Forgings & Extrusions; A (TB00) Temper (UNS C17500) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 10 Plate & Rolled Bar; A (TB00) Temper; All Thicknesses (UNS C17500) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
Zoltek Pyron® Continuous Tow Oxidized Pan Fiber Oxidized Pan FiberApplications include: Yarn Stretch Breaking, Pulp Milling, Staple Fiber Chop for Nonwovens or Yarn Spinning |
|||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | dry; ISO 527-1/-2 |
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TW200B6 PA46-CF30 30% Carbon Reinforced, Heat Stabilized, Lubricated |
|||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TW272B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 240 MPa @Temperature 200 °C |
34800 psi @Temperature 392 °F |
Typical, after 10,000 hours |
Aleris Weldural Aluminum Alloy, 100 mm Thickness Sample treatment not specified for property data.Applications include precise mechanical parts with high dimensional stability, machine components, molds, and refrigeration engineering. Good weldab.. |
|||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | dry; ISO 527-1/-2 |
DSM Novamid® MC112LG55 C10 PA6-GF55 55% Glass Reinforced |
|||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | ISO 527 |
LATI LARAMID G/50 50% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s.. |
|||
Tensile Strength, Ultimate | 240 - 380 MPa | 34800 - 55100 psi | |
Materion Beryllium Copper Alloy 3 Tube; A (TB00) Temper; All Sizes (UNS C17510) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |