Polymer Property : Tensile Strength, Ultimate = 3480 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
NCMT NanoPAC™ HS403 High Performance Polypropylene Nanocomposite Applications: Electrical AppliancesInformation provided by Nano Composite Materials Technology Limited
Tensile Strength, Ultimate	24.0 MPa	3480 psi
Reliance Industries BIOMER P226 compared to PPInformation provided by Reliance Industries
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
Reliance Industries Relene L41003 Polyethylene The UV stabilized version of Relene E41003Information provided by Reliance Industries
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
Solvay Specialty Polymers Algoflon® 20FLCA PTFE; Calcium Fluoride Filled (discontinued **) Data provided by the manufacturer.20 wt.% Calcium Fluoride. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric properties, ..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
Ineos ABS Centrex® 401 AES Extrusion (discontinued **) Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
ExxonMobil Iotek® 7610 Zinc Ionomer (discontinued **) Data provided by the manufacturer, Exxon Chemical.A low melt index zinc ionomer made from an ethylene acrylic acid base polymer. It is designed to have high durability, resilience and impact streng..
Tensile Strength, Ultimate	24.0 MPa @Temperature 60.0 °C	3480 psi @Temperature 140 °F	ISO 527
LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound (Unverified Data**) Description: These are compounds containing a high percentage of magnetizable fillers; compared to traditional techniques for the manufacture of magnets, this allows the molding of complex shapes us..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	Compounded Tire
Polynorbornene Rubber (PNR) High glass temperature - plasticizer needed to make a 'rubbery' compound.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
IDI Composites 46-3 Thermoset Polyester, Molding Superior electrical performance with low pressure molding for V-O flammability in encapsulation applications.Data provided by the manufacturer.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
Ineos Styrenics AvantraÂ® 585K Q402 Rubber Modified Polystyrene AvantraÂ® 585K Q402 is a high-impact grade of polystyrene with extremely high surface gloss and excellent practical toughness. Although AvantraÂ® 585K Q402 can be processed by any method applic..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
Ineos Styrenics AvantraÂ® 585K Rubber Modified Polystyrene AvantraÂ® 585K is a high-impact grade of polystyrene with extremely high surface gloss and excellent practical impact strength. Although AvantraÂ® 585K can be processed by any method applicable..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	at max load; ISO 527
A. Schulman FORMION™ FI 401 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	at max load; ISO 527
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	at max load; ISO 527
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	at max load; ISO 527
A. Schulman FORMION™ FI 401 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	at max load; ISO 527
A. Schulman FORMION™ FI 372 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	at max load; ISO 527
A. Schulman FORMION™ FI 401 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ISO 37
Lubrizol ESTANE® GP70AE Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability ..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	at max load; ISO 527
A. Schulman FORMION™ FI 401 Ionomer Information provided by A. Schulman.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
Covestro Bayflex® 110-50 Polyurethane Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638/D412
Covestro Bayflex® XGT-50 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ISO 527
Dow INSPIRE™ 112 Performance Polymer INSPIRE™ 112 Performance Polymer is a propylene-based resin intended for use in film and sheet extrusion.Information provided by Dow
Tensile Strength, Ultimate	24.0 - 27.0 MPa	3480 - 3920 psi
Biomer P226 PHB Biodegradable Polymer PHB is a isotactic, absolutely linear, thermoplastic homopolyester built of 3-hydroxy butyric acid. The formula of the subunit is -[O-CH(CH3)-CH2-CO]-. PHB is free from even traces of catalysts. P..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	Dynamic tensile strength
Channel Industries 600 Barium Titanate Piezoelectric Modified barium titanates are widely used in transducers requiring moderate power level and receiving sensitivity. Special characteristics have made barium titanate a proven material for use in devi..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
Solvay Specialty Polymers Algoflon® 15GL PTFE; Glass Fiber Filled (discontinued **) Data provided by the manufacturer.15 wt.% Glass Fiber. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric properties, almos..
Tensile Strength, Ultimate	24.0 - 102 MPa @Strain 2.00 - 30.0 %	3480 - 14800 psi @Strain 2.00 - 30.0 %	Average value: 53.1 MPa Grade Count:3
Overview of materials for Thermoplastic Polyurethane (TPUR), Polyester Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Polyester Grade". Each property range of values reported is minimum a..
Tensile Strength, Ultimate	24.0 - 102 MPa @Temperature 0.000 - 60.0 °C	3480 - 14800 psi @Temperature 32.0 - 140 °F	Average value: 54.9 MPa Grade Count:3
Overview of materials for Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced". Each property range of values reported is mi..
Tensile Strength, Ultimate	24.0 - 102 MPa @Strain 2.00 - 30.0 %	3480 - 14800 psi @Strain 2.00 - 30.0 %	Average value: 54.9 MPa Grade Count:3
Overview of materials for Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced". Each property range of values reported is mi..
Tensile Strength, Ultimate	24.0 MPa	3480 psi	ASTM D638
ExxonMobil Iotek® 7310 Zinc Ionomer (discontinued **) Data provided by the manufacturer, Exxon Chemical.A low melt index zinc ionomer made from an ethylene acrylic acid base polymer.Applications: Injection molding; Impact modifier of polyamide.
Tensile Strength, Ultimate	24.0 MPa	3480 psi	50 mm/min; ASTM D638
LyondellBasell INDURE™ X210 TPO Description: INDURE™ X210 engineered polyolefin material is designed for large automotive exterior applications that require ductile impact properties at low temperatures, and processability. Appli..