Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 8620 BLK Formulated TPE compound is based on Shell's Kraton G resin and is widely used in automotive applications exhibiting a wide temperature range, replacing in many applications conventional thermoset ru.. |
|||
Tensile Strength, Ultimate | 10.3 - 14.5 MPa | 1490 - 2100 psi | ASTM D638 |
Multibase Multi-Flex® TPE D 4107 This product is UV stabilized for automotive applications, like fender guards and airbags. The Xenon Arc is 2.5 Delta E, ASTM SAE J1960 1240 KJ/m². Passes Impact resistance test ASTM GM 9032 P at.. |
|||
Tensile Strength, Ultimate | >= 10.3 MPa | >= 1490 psi | ASTM D412 |
Multibase Multi-Flex® TPE G 7680 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 10.3 - 14.5 MPa | 1490 - 2100 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO 1047-4107 Passed impact resistance 3.4J at -30°C; ASTM GM 9032 P. This product is UV stabilized for automotive applications, like fender guards and airbags.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | post cured- 4 hours at 204°C |
Multibase SILASTIC® C7-4550 TBPB Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | ASTM D638 |
ExxonMobil Escorene® LD-411 LDPE Power Cable Insulation
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A crosslinkable polyethylene homopolymer designed as an electrical grade base resin especially suitable for Henschel blending.Applications: A base r.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman M3019-P Polyethylene
(discontinued **) M3019-P is suggested for applications such as spiral-wound can linings, release paper, and photographic paper. M3019-P Has been found to exhibit good barrier properties, temperature resistance, and.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | ASTM D3574E |
Mearthane Durethaneâ„¢ F DF-225A Closed Cell Foam Polyurethane TDI backbone: ester.Shore 00 Hardness: 70Summary: Durethane F is chemically blown urethane closed cell foam. Mearthane can custom formulate Durethane F, varying the physical properties (coefficient.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | |
Kuraray SEPTON® H5127 Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | |
Kuraray HYBRAR® SC1 Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 10.3 MPa @Treatment Temp. 150 °C, Time 605000 sec |
1490 psi @Treatment Temp. 302 °F, Time 168 hour |
Heat Aging; ASTM D 412/ASTM D 573 |
Zylog Neoplast® 180 C Thermoplastic Vulcanizate Neoplast 180 C is a soft, dynamically vulcanized thermoplastic vulcanizate (TPV), based on polyolefin chemistry, and is intended for Injection Molding and Extrusion applications.RoHS Compliant, UV S.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8100 Polyolefin Elastomer Description: Engage® 8100 polyolefin elastomer is an ethyleneoctene copolymer that has excellent flow characteristics and performs well in a wide range of general purpose thermoplastic elastomer ap.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8107 Polyolefin Elastomer Description: Engage® 8107 polyolefin elastomer is a loose talc surface coated ethylene-octene copolymer. The talc is untreated and has a nominal 1µm particle size. This product offers the exceptio.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | |
Dow HDPE 42047N High Density Polyethylene DOW HDPE 42047N resin is a narrow molecular weight distribution copolymer designed to combine high impact strength and environmental stress crack resistance with excellent processability over a wide.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | |
Dow HDPE 65053N High Density Polyethylene DOW HDPE 65053N resin is a narrow molecular weight distribution copolymer designed to offer good environmental stress crack resistance and rigidity with high impact strength. This resin has excellen.. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | |
Dow LDPE 4005M Low Density Polyethylene Data provided by Dow Chemical. |
|||
Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | DOWM 100789-LE90A |
Dow Tyrin® CM674 Elastomer Formulation FormulationTyrin® CPE Elastomer |
|||
Tensile Strength, Ultimate | 10.3 MPa @Thickness 1.14 - 1.52 mm, Temperature 816 °C |
1490 psi @Thickness 0.0449 - 0.0598 in, Temperature 1500 °F |
|
AK Steel 409 Ferritic Stainless steel AK Steel 409 Stainless Steels are especially useful for applications where oxidation or corrosion protection beyond the capacity of carbon steel and some coated steels is needed. Current applicatio.. |