- Polymer Property : Tensile Strength, Ultimate = 142000 psi
Polymer Property : Tensile Strength, Ultimate = 142000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 976 MPa | 142000 psi | |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Tensile Strength, Ultimate | 982 MPa | 142000 psi | |
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| Tensile Strength, Ultimate | 981 MPa | 142000 psi | at Surface, Longitudinal |
| International Mold Steel P20 Plastic Mold Steel P20 tool steel is 28 – 32 HRC (Din # 1.2738). Features better hardenability than AISI P20 due to the addition of nickel.
Information provided by International Mold Steel. |
|||
| Tensile Strength, Ultimate | 981 MPa | 142000 psi | at Surface, Transverse |
| International Mold Steel P20 Plastic Mold Steel P20 tool steel is 28 – 32 HRC (Din # 1.2738). Features better hardenability than AISI P20 due to the addition of nickel.
Information provided by International Mold Steel. |
|||
| Tensile Strength, Ultimate | 981 MPa | 142000 psi | at Surface, Longitudinal |
| International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure – no pin holes, inclusions or hard spots. 30-3.. |
|||
| Tensile Strength, Ultimate | 981 MPa | 142000 psi | at Surface, Transverse |
| International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure – no pin holes, inclusions or hard spots. 30-3.. |
|||
| Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
| Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Tensile Strength, Ultimate | >= 981 MPa | >= 142000 psi | |
| Crucible Steel MCU Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | 979 MPa | 142000 psi | |
| Carpenter Custom 450® Stainless Steel, Annealed Data provided by Carpenter Technology Corporation.Custom 450® stainless is a martensitic age-hardenable stainless steel which exhibits very good corrosion resistance (similar to that of Stainless T.. |
|||
| Tensile Strength, Ultimate | 979 MPa | 142000 psi | |
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, 40% Cold Rolled (UNS S30500) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| Tensile Strength, Ultimate | 980 - 1100 MPa | 142000 - 160000 psi | |
| ArcelorMittal Dual Phase 980 LCE Y660 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
| Tensile Strength, Ultimate | 979 MPa | 142000 psi | |
| Carpenter Custom 450® Stainless Steel, Condition H1150 (Age Hardened 621°C) Data provided by Carpenter Technology Corporation.Custom 450® stainless is a martensitic age-hardenable stainless steel which exhibits very good corrosion resistance (similar to that of Stainless T.. |
|||
| Tensile Strength, Ultimate | 979 MPa @Thickness 25.4 mm, Temperature 200 °C |
142000 psi @Thickness 1.00 in, Temperature 392 °F |
R<sub>m</sub>. Bar. 310 HB |
| Assab Steels 618 Plastic Mold Material ASSAB 618 is a vacuum-degassed Cr-Ni-Mo-alloy steel which is supplied in the hardened and tempered condition. ASSAB 618 is manufactured to consistently high quality standards with a controlled sulfu.. |
|||
| Tensile Strength, Ultimate | 979 MPa @Thickness 25.4 mm, Temperature 200 °C |
142000 psi @Thickness 1.00 in, Temperature 392 °F |
R<sub>m</sub>. Bar. 310 HB |
| Assab Steels 718HH Plastic Mold Material IMPAX SUPREME is a premium-quality vacuum-degassed Cr-Ni-Mo-alloyed steel which is supplied in the hardened and tempered condition. IMPAX SUPREME is manufactured to consistently high quality standar.. |
|||
| Tensile Strength, Ultimate | 980 - 1200 MPa | 142000 - 174000 psi | |
| ArcelorMittal Complex Phase Steel 1000 SF Very high strength steel, Cold Rolled Steel Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels are cold formed to make lightweight structural elements. A num.. |
|||
| Tensile Strength, Ultimate | 980 - 1200 MPa | 142000 - 174000 psi | |
| ArcelorMittal Complex Phase Steel 1000 Very high strength steel, Cold Rolled Steel Available in the following: uncoated (HCT980C) and electrogalvanized (HCT980C+ZE)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product r.. |
|||
| Tensile Strength, Ultimate | 980 - 1130 MPa | 142000 - 164000 psi | |
| ArcelorMittal Complex Phase Steel 1000 Y800 Very high strength steel, Cold Rolled Steel Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels are cold formed to make lightweight structural elements. A num.. |
|||
| Tensile Strength, Ultimate | 980 - 1100 MPa | 142000 - 160000 psi | |
| ArcelorMittal Dual Phase 1180 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
| Tensile Strength, Ultimate | 980 - 1100 MPa | 142000 - 160000 psi | |
| ArcelorMittal Dual Phase 980 LCE Y700 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
| Tensile Strength, Ultimate | 980 - 1100 MPa | 142000 - 160000 psi | |
| ArcelorMittal Dual Phase 980 Y700 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
| Tensile Strength, Ultimate | 980 MPa | 142000 psi | |
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Tensile Strength, Ultimate | 978 MPa @Treatment Temp. 871 °C, Time 5.76e+7 sec |
142000 psi @Treatment Temp. 1600 °F, Time 16000 hour |
Room temp test after thermal exposure |
| Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||
| Tensile Strength, Ultimate | 979 MPa | 142000 psi | |
| Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 0% Cold Work Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough®.. |
|||