Polymer Property : Tensile Strength, Ultimate = 1080 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	>= 7.45 MPa	>= 1080 psi	ASTM D412
Multibase Multi-Flex® TPE A 7606 BLK The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 7.45 MPa	>= 1080 psi	ASTM D412
Multibase Multi-Flex® TPE A 7606 GRAPHITE The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 7.45 MPa	>= 1080 psi	ASTM D412
Multibase Multi-Flex® TPE A 7606 JA6A BLK The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	7.45 MPa	1080 psi	post cured- 8 hours at 200°C; ASTM D412
Multibase SILASTIC® Q7-4840 Dow-Corning Biomedical Grade Liquid Silicone Rubber Information provided by Multibase
Tensile Strength, Ultimate	7.45 MPa @Time 605000 sec	1080 psi @Time 168 hour	Heat Aging; ASTM D 412/ASTM D 573
Zylog Neoplast® 163 FT EB Thermoplastic Vulcanizate Neoplast 163 FT EB is a soft, dynamically vulcanized thermoplastic vulcanizate (TPV), based on polyolefin chemistry, and is intended for Injection Molding, Blow Molding and Extrusion applications.Ro..
Tensile Strength, Ultimate	7.45 MPa	1080 psi
Dow Corning SILASTIC® P-1 RTV SILICONE RUBBER & BLUE CURING AGENT High strength silicone rubber suited for prototyping, production tooling, artistic and renovation applications. Silastic P-1 is recommended for use with polyesters, cement and rigid polyurethanes; a..
Tensile Strength, Ultimate	7.45 MPa	1080 psi
Dow Corning SILASTIC® P-1 RTV SILICONE RUBBER & CLEAR CURING AGENT High strength silicone rubber suited for prototyping, production tooling, artistic and renovation applications. Silastic P-1 is recommended for use with polyesters, cement and rigid polyurethanes; a..
Tensile Strength, Ultimate	7.47 - 9.13 MPa	1080 - 1320 psi
Arlon Thermavac® 0.040" (0.762 mm) Cured Silicone Vacuum Bagging (10502R040) Unsupported cured/post cured silicone rubber with a thickness of 0.040 in. ±0.004 (1.0 mm ±0.10); 0.003 in. (0.8 mm) polyethylene interleave. The shelf life is defined as the duration of time for..
Tensile Strength, Ultimate	7.47 - 9.13 MPa	1080 - 1320 psi
Arlon Thermavac® 0.060" (1.524 mm) Cured Silicone Vacuum Bagging (10502N060) Unsupported cured/post cured silicone rubber with a thickness of 0.060 in. ±0.006 (1.5 mm ±0.15 ); 0.003 in. (0.8 mm) polyethylene interleave. Color: Translucent. Weight: 2339 g/m² ± 234 (69.0..
Tensile Strength, Ultimate	7.47 - 9.13 MPa	1080 - 1320 psi
Arlon Thermavac® 0.060" (1.524 mm) Cured Silicone Vacuum Bagging (10502R060) Unsupported cured/post cured silicone rubber with a thickness of 0.060 in. ±0.006 (1.5 mm ±0.15); 0.003 in. (0.8 mm) polyethylene interleave. The shelf life is defined as the duration of time for..
Tensile Strength, Ultimate	7.45 - 21.0 MPa	1080 - 3050 psi	Average value: 13.1 MPa Grade Count:7
Overview of materials for Linear Low Density Polyethylene (LLDPE), Compounding Resin This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Compounding Resin". Each property range of values reported is m..