Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 18.0 - 18.0 MPa @Temperature 60.0 - 60.0 °C |
2610 - 2610 psi @Temperature 140 - 140 °F |
Average value: 18.0 MPa Grade Count:1 |
Overview of materials for Polystyrene, Heat Resistant Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Heat Resistant Grade". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 7.00 - 18.0 MPa | 1020 - 2610 psi | |
ATG s.r.l. BR Polybutadiene Rubber |
|||
Tensile Strength, Ultimate | 9.00 - 18.0 MPa | 1310 - 2610 psi | |
ATG s.r.l. EACM Ethylene-Acrylic Rubber |
|||
Tensile Strength, Ultimate | 6.00 - 18.0 MPa | 870 - 2610 psi | |
ATG s.r.l. EPDM Ethylene-Propylene Terpolymer |
|||
Tensile Strength, Ultimate | 6.00 - 18.0 MPa | 870 - 2610 psi | |
ATG s.r.l. EPM Ethylene-Propylene Copolymer |
|||
Tensile Strength, Ultimate | 7.00 - 18.0 MPa | 1020 - 2610 psi | |
ATG s.r.l. IIR Butyl Rubber |
|||
Tensile Strength, Ultimate | 9.00 - 18.0 MPa | 1310 - 2610 psi | Average value: 11.4 MPa Grade Count:28 |
Overview of materials for Low Density Polyethylene (LDPE), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Extrusion Grade". Each property range of values reported is minimum and.. |
|||
Tensile Strength, Ultimate | 10.3 - 18.0 MPa | 1500 - 2610 psi | Average value: 14.1 MPa Grade Count:23 |
Overview of materials for Low Density Polyethylene (LDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Blow Molding Grade". Each property range of values reported is minimum .. |
|||
Tensile Strength, Ultimate | 7.00 - 18.0 MPa @Temperature 60.0 - 120 °C |
1020 - 2610 psi @Temperature 140 - 248 °F |
Average value: 12.3 MPa Grade Count:1 |
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are.. |