Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 50.0 - 130 MPa @Temperature -20.0 - 100 °C |
7250 - 18900 psi @Temperature -4.00 - 212 °F |
Average value: 53.1 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% .. |
|||
Tensile Strength, Ultimate | 50.0 - 130 MPa @Temperature 125 - 275 °C |
7250 - 18900 psi @Temperature 257 - 527 °F |
Average value: 86.7 MPa Grade Count:1 |
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i.. |
|||
Tensile Strength, Ultimate | 73.0 - 130 MPa | 10600 - 18900 psi | Average value: 106 MPa Grade Count:4 |
Overview of materials for PCT, 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT, 40% Glass Reinforced". Specific grades with glass content between 35% and 44% are included. Each pr.. |
|||
Tensile Strength, Ultimate | 57.0 - 130 MPa | 8270 - 18900 psi | Average value: 104 MPa Grade Count:23 |
Overview of materials for PBT + ASA Blend, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PBT + ASA Blend, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum .. |
|||
Tensile Strength, Ultimate | 86.0 - 130 MPa | 12500 - 18900 psi | Average value: 111 MPa Grade Count:16 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%.. |
|||
Tensile Strength, Ultimate | 130 - 130 MPa @Temperature 130 - 175 °C |
18900 - 18900 psi @Temperature 266 - 347 °F |
Average value: 147 MPa Grade Count:1 |
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. .. |
|||
Tensile Strength, Ultimate | 130 - 130 MPa @Time 1.80e+7 - 7.20e+7 sec |
18900 - 18900 psi @Time 5000 - 20000 hour |
Average value: 147 MPa Grade Count:1 |
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. .. |
|||
Tensile Strength, Ultimate | 44.0 - 130 MPa | 6380 - 18900 psi | Average value: 66.4 MPa Grade Count:15 |
Overview of materials for Nylon 612, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Unreinforced". Each property range of values reported is minimum and maximum values of approp.. |
|||
Tensile Strength, Ultimate | 20.0 - 130 MPa @Temperature -40.0 - 120 °C |
2900 - 18900 psi @Temperature -40.0 - 248 °F |
Average value: 58.7 MPa Grade Count:11 |
Overview of materials for Nylon 6, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum v.. |
|||
Tensile Strength, Ultimate | 120 - 130 MPa @Temperature 130 - 180 °C |
17400 - 18900 psi @Temperature 266 - 356 °F |
Average value: 98.0 MPa Grade Count:5 |
Overview of materials for Polyphthalamide (PPA), Glass Fiber 40% This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Glass Fiber 40%". Specific grades with glass content between 35% and 44% are included. .. |
|||
Tensile Strength, Ultimate | 120 - 130 MPa @Time 1.80e+7 - 7.20e+7 sec |
17400 - 18900 psi @Time 5000 - 20000 hour |
Average value: 98.0 MPa Grade Count:5 |
Overview of materials for Polyphthalamide (PPA), Glass Fiber 40% This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Glass Fiber 40%". Specific grades with glass content between 35% and 44% are included. .. |
|||
Tensile Strength, Ultimate | 6.89 - 130 MPa | 1000 - 18900 psi | Average value: 80.8 MPa Grade Count:184 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |
|||
Tensile Strength, Ultimate | 0.750 - 130 MPa | 109 - 18900 psi | Average value: 13.4 MPa Grade Count:541 |
Overview of materials for Thermoset Fluoroelastomer This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Fluoroelastomer". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Ultimate | 40.7 - 130 MPa | 5900 - 18900 psi | Average value: 66.1 MPa Grade Count:38 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Bead Filled". Each property range of values reported is minimum .. |