- Polymer Property : Tensile Strength, Ultimate = 862 MPa
Polymer Property : Tensile Strength, Ultimate = 862 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| Pacific Sintered Materials FX-233-T(HT) Infiltrated Alloy Steel Excellent combination of strength and shock resistance. Good for use in cams, pawls, sprockets and wear plates. Moderate tolerance control.All information provided by Pacific Sintered Metals. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| PSM Industries Pacific Sintered Metals Infiltrated Alloy Steel FX-233-T(HT) Powdered Metal Excellent combination of strength and shock resistance, Good for use in cams, pawls, sprockets and wear plates, Moderate tolerance controlInformation Provided by Pacific Sintered Metals, a division .. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | 3 inches; Un-Nitrided |
| Latrobe LSSâ„¢ 135M Nitriding Steel (ASTM A355 Class A) TLS 135M Nitriding Steel is a high-aluminum and chromium modification of AISI 4140 alloy steel. The aluminum addition promotes the formation of aluminum nitride compounds when tools manufactured fr.. |
|||
| Tensile Strength, Ultimate | >= 862 MPa @Thickness <=0.400 mm |
>= 125000 psi @Thickness <=0.0157 in |
CWSR, 0.016 in. Wall & Below; AMS 4944/4945 |
| Haynes Ti-3Al-2.5V Alloy Titanium Tubing Haynes® Ti-3Al-2.5V alloy is both lightweight and strong, providing a major design advantage - saving weight.Specific alloying additives, notably aluminum, raise the temperature at which a titani.. |
|||
| Tensile Strength, Ultimate | >= 862 MPa @Thickness >=0.400 mm |
>= 125000 psi @Thickness >=0.0157 in |
CWSR, Above 0.016 in. Wall; AMS 4944/4945 |
| Haynes Ti-3Al-2.5V Alloy Titanium Tubing Haynes® Ti-3Al-2.5V alloy is both lightweight and strong, providing a major design advantage - saving weight.Specific alloying additives, notably aluminum, raise the temperature at which a titani.. |
|||
| Tensile Strength, Ultimate | 862 MPa @Temperature 538 °C |
125000 psi @Temperature 1000 °F |
|
| Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| HP Alloys Alloy 718, 0% Cold Worked, Not Aged 0% Cold Worked, Not Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes .. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| Schmolz + Bickenbach MoldMAX® V Copper Alloy Description: Brush Wellman’s MoldMAX® V (MMV) is a high conductivity, moderately high strength, copper nickel silicon chromium alloy. Applications include injection mold and blow mold cores .. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | Typical |
| TIMET TIMETAL® 5111 Titanium Alloy (Ti-5Al-1Sn-1Zr-1V-0.8Mo; ASTM Grade 32) High Toughness, Heavy Section Weldable AlloyFeatures: A near alpha alloy with excellent weldability, seawater stress corrosion cracking resistance and high dynamic toughness. It is ideally suited f.. |
|||
| Tensile Strength, Ultimate | 862 MPa @Temperature 23.0 °C |
125000 psi @Temperature 73.4 °F |
|
| Crucible Compaction Metals P/M N690 Corrosion Resistant Alloy P/M N690 (chemically, UNS N06690) is produced by the state-of-the-art Crucible P/M process: inert gas atomization, coupled with consolidation by hot isostatic pressing and/or extrusion. The advance.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | H1150-M |
| Crucible Steel 15-5 Precipitation Hardening Stainless Steel Crucible 15-5 is a Premium Quality precipitation-hardening stainless steel which is capable of high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is a V.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | H1150-M |
| Crucible Steel 17Cr-4Ni Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a precipitation-hardening stainless steel which is capable of a high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is martensitic a.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| CMW® 3000 AMS-T-21014 AMS-7725 High Density Machinable Tungsten Uses: Radiation Shielding, High Mass, Gyro, Ordnance. Machinability is similar to gray iron.Information provided by CMW Inc. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| CMW® 3970 AMS-T-21014 ASTM B777 High Density Machinable Tungsten Uses: Radiation Shielding, High Mass, Gyro, OrdnanceInformation provided by CMW Inc. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| Crucible Steel 431 Chromium Steel Crucible 431 is a nickel bearing chromium steel which can be treated to exceptionally high physical properties. In the heat treated conditions, its corrosion resistance is superior to similar marten.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| Crucible Steel 431 Chromium Steel Crucible 431 is a nickel bearing chromium steel which can be treated to exceptionally high physical properties. In the heat treated conditions, its corrosion resistance is superior to similar marten.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | cold worked |
| CMW® ELKONIUM 302 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| CMW® THERMKON® 62 Tungsten Copper parts For matching CTE of semiconductor substrates while allowing high thermal transfer.Information provided by CMW Inc. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | Cold-Worked 1/4 hard |
| AK Steel 201 Austenitic Stainless steel AK Steel 210 was developed originally to conserve nickel. It provides properties similar to Type 301 and can be used in most applications for Type 301. This alloy is non-magnetic in the annealed c.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | Cold-Worked 1/4 hard |
| AK Steel 301 Austenitic Stainless steel AK Steel 301 provides high strength and good ductility when cold worked. It is a modification of AK Steel 302 to increase the cold work-hardening range, to permit higher tensile strengths to be ach.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 35% Cold Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Vacuum arc remelted (VAR), low carbon version of Type 316 stainless. The secondary premium melting step (VAR) imparts impro.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | 0% Cold Work |
| AK Steel NITRONIC® 30 Austenitic Stainless Steel AK Steel NITRONIC 30 Stainless Steel offers significantly higher strength than Type 304 and potential for applications requiring good resistance to aqueous and atmospheric corrosion resistance combi.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| ATI Allvac® 6-4ELI Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal Data provided by Allvac.Applications: Applications requiring excellent fracture toughness and fatigue strength; aircraft, structural components, biomedical. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| ATI Allvac® 6-7 UNS R56700 Titanium Alloy Uses: Biomedical implants. Femoral hip stems, fracture fixation plates, spinal components, fasteners, nails, rods, screws, wire.Property values are for samples in the metallurgical condition: 1300°.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| ATI Allvac® Nickelvac® H-B-2 UNS N10665 Nickel Superalloy Vessels, pumps, valves, piping systems for the production of hydrochloric, sulfuric, acetic, and phosphoric acids.Property values are for samples in the metallurgical condition: 1600°F age.Informat.. |
|||
| Tensile Strength, Ultimate | >= 862 MPa | >= 125000 psi | |
| ATI Allegheny Ludlum Stainless Steel Type 301, 1/4 Hard (UNS S30100) Allegheny Ludlum Type 301 is a high strength grade of steel available in six conditions or tempers, its resistance to atmosphere corrosion and its bright, attractive surface make it an excellent cho.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, 30% Cold Rolled (UNS S30500) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| Tensile Strength, Ultimate | >= 862 MPa | >= 125000 psi | |
| Materion ToughMet® T3 AT110 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin.. |
|||
| Tensile Strength, Ultimate | 862 MPa | 125000 psi | |
| Latrobe Nitralloy® 135 Modified VAC-ARC, 1.5 to 3 in Premium Nitriding Steel NITRALLOY 135 MODIFIED VAC-ARC steel is a low alloy nitriding grade with moderate hardenability. It has been designed to provide a high case hardness and to maintain its core strength during the nit.. |
|||