Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 7.00 - 23.0 MPa | 1020 - 3340 psi | Average value: 10.5 MPa Grade Count:8 |
Overview of materials for Polytetrafluoroethylene (PTFE), Mica Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Mica Filled". Each property range of values reported is minimum and maxi.. |
|||
Tensile Strength, Ultimate | 7.00 - 17.0 MPa @Temperature 250 - 250 °C |
1020 - 2470 psi @Temperature 482 - 482 °F |
Average value: 11.0 MPa Grade Count:8 |
Overview of materials for Polyperfluoroalkoxyethylene (PFA), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyperfluoroalkoxyethylene, Molded/Extruded". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 7.00 MPa | 1020 psi | Original Properties; ASTM D412 Die C |
Freudenberg Simrit S40 Silicone Elastomer (VMQ) General Purpose; AMS 3301; A-A-59588 (ZZ-R-765) Class 2A, 2B Grade 40; Good heat resistance. Poor resistance to abrasion, tear and cut growth; low tensile strength; inferior resistance to oil, gasol.. |
|||
Tensile Strength, Ultimate | 7.00 MPa | 1020 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4770P Highly Extended Low-Cost Hose FormulationNordel® IP 4770P |
|||
Tensile Strength, Ultimate | 7.00 MPa | 1020 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4770R Highly Extended Low-Cost Hose FormulationNordel® IP 4770R |
|||
Tensile Strength, Ultimate | 7.00 - 18.0 MPa | 1020 - 2610 psi | |
ATG s.r.l. BR Polybutadiene Rubber |
|||
Tensile Strength, Ultimate | 7.00 - 24.0 MPa | 1020 - 3480 psi | |
ATG s.r.l. CR Polychloroprene |
|||
Tensile Strength, Ultimate | 7.00 - 18.0 MPa | 1020 - 2610 psi | |
ATG s.r.l. IIR Butyl Rubber |
|||
Tensile Strength, Ultimate | 7.00 - 25.0 MPa | 1020 - 3630 psi | |
ATG s.r.l. NBR Nitrile-Butadiene Rubber |
|||
Tensile Strength, Ultimate | 7.00 - 28.0 MPa | 1020 - 4060 psi | |
ATG s.r.l. SBR Styrene-Butadiene Rubber |
|||
Tensile Strength, Ultimate | 7.00 MPa @Temperature 250 °C |
1020 psi @Temperature 482 °F |
ASTM D638 |
Asahi Glass Fluon® P-62XP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength, Ultimate | 7.00 MPa @Temperature 250 °C |
1020 psi @Temperature 482 °F |
ASTM D638 |
Asahi Glass Fluon® P-830UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength, Ultimate | 7.00 MPa | 1020 psi | ASTM D638 |
Toyobo Pelprene™ P-30B Polyester TPE Key Feature: Pelprene P typePelprene™ can be processed into a wide variety of articles from ultra-small precision parts to sheets by injection, extrusion, and blow molding. The 'P' type is a block.. |
|||
Tensile Strength, Ultimate | 7.00 - 57.0 MPa | 1020 - 8270 psi | Average value: 27.1 MPa Grade Count:69 |
Overview of materials for Polyether Ester Elastomer This property data is a summary of similar materials in the MatWeb database for the category "Polyether Ester Elastomer". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Ultimate | 7.00 - 45.0 MPa @Temperature 60.0 - 90.0 °C |
1020 - 6530 psi @Temperature 140 - 194 °F |
Average value: 16.9 MPa Grade Count:4 |
Overview of materials for Polypropylene, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Flame Retardant". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 7.00 - 18.0 MPa @Temperature 60.0 - 120 °C |
1020 - 2610 psi @Temperature 140 - 248 °F |
Average value: 12.3 MPa Grade Count:1 |
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are.. |
|||
Tensile Strength, Ultimate | 7.00 - 16.0 MPa @Temperature 60.0 - 120 °C |
1020 - 2320 psi @Temperature 140 - 248 °F |
Average value: 11.4 MPa Grade Count:4 |
Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |