Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 6.00 MPa | 870 psi | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 |
Eastman 812A Polyethylene
(discontinued **) Polyethylene 812A is a natural low density material with a 200 melt index. This high-flow formulation is used for specialty injection molding applications in the medical market.Unless otherwise not.. |
|||
Tensile Strength, Ultimate | 6.00 - 185 MPa | 870 - 26800 psi | Average value: 86.9 MPa Grade Count:161 |
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Ultimate | 6.00 MPa | 870 psi | |
Dow Corning HV 1520/40 40 Shore Hardness Conductive liquid silicone rubber with high tear strength, high electrical conductivity and fast cure speedInformation provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.00 MPa | 870 psi | |
Dow Corning SILASTIC® 9251/45 A&B KIT 45 Durometer, 2-part, 1 to 1 mix, off-white, Fabric Coating grade, Liquid Silicone Rubber.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.00 MPa | 870 psi | |
Dow Corning SILASTIC® 9252/500P PARTS A&B Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.00 - 15.0 MPa | 870 - 2180 psi | |
ATG s.r.l. CO-ECO Epichlorohydrin Rubber |
|||
Tensile Strength, Ultimate | 6.00 - 18.0 MPa | 870 - 2610 psi | |
ATG s.r.l. EPDM Ethylene-Propylene Terpolymer |
|||
Tensile Strength, Ultimate | 6.00 - 18.0 MPa | 870 - 2610 psi | |
ATG s.r.l. EPM Ethylene-Propylene Copolymer |
|||
Tensile Strength, Ultimate | 6.00 - 10.0 MPa | 870 - 1450 psi | |
ATG s.r.l. FVMQ Fluorosilicone Rubber |
|||
Tensile Strength, Ultimate | 6.00 - 9.00 MPa | 870 - 1310 psi | |
ATG s.r.l. PVMQ Silicone Rubber |