Polymer Property : Fatigue Strength = 290 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Fatigue Strength	290 - 330 MPa @# of Cycles 1.00e+8	42100 - 47900 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 190 Strip; 1/2HM (TM02) Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 67%Formability Ratio, 90Â° Bend, R..
Fatigue Strength	290 - 320 MPa @# of Cycles 1.00e+8	42100 - 46400 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 25 Strip; 1/2HT (TH02) Temper (UNS C17200) Treatment required for max strength: 2 hrs @ 315ÂºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 73%Superficial Hardness: 30N 58-6..
Fatigue Strength	290 - 330 MPa @# of Cycles 1.00e+8	42100 - 47900 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM02 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 76%Formability Ratio, 90Â° Bend, R..
Fatigue Strength	290 MPa @# of Cycles 1.00e+8	42000 psi @# of Cycles 1.00e+8	rotating beam
Dura-Bar 65-45-12 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for..
Fatigue Strength	290 MPa @# of Cycles 1.00e+7	42000 psi @# of Cycles 1.00e+7	Unnotched
ATI Wah Chang Zircadyne® Alloy Zr 705 Zircadyne 705 is zirconium alloyed with niobium to increase its strength and improve its formability. Alloy exhibits good ductility even at cryogenic temperatures and strength comparable with other ..
Fatigue Strength	290 - 320 MPa @# of Cycles 1.00e+8	42100 - 46400 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 3 Strip; HT (TH04) Temper (UNS C17510) Treatment required for max strength: 2-3 hrs @ 480ºC or Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 96%Stress Relaxation after 1000 hrs @ 200°C: 75%Formability Ratio..