Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 50.0 MPa @Temperature 250 °C |
7250 psi @Temperature 482 °F |
ISO 604 |
Victrex® PEEK -HT™ 22GL30 Polyetherketone, 30% Glass Fiber Reinforced Product Description:High performance thermoplastic material, 30% glass fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact comp.. |
|||
Compressive Strength | 50.0 MPa @Temperature 250 °C |
7250 psi @Temperature 482 °F |
ISO 604 |
Victrex® ST™ ST45GL30 Polyetherketoneetherketoneketone (PEKEKK), 30% Glass Fiber Reinforced Product Description:High performance thermoplastic material, 30% glass fibre reinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, granules for injection moulding, standard flow, c.. |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 100 °C |
7250 - 8700 psi @Temperature 212 °F |
Cold Crushing Strength |
Gouda Vuurvast CURON 160 Dense Refractory Castable Description: Because of the selection of raw materials this castable has a high volume stability and maintains its strength up to high temperatures. In addition Curon 160 has an excellent thermal sh.. |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 100 °C |
7250 - 8700 psi @Temperature 212 °F |
Cold Crushing Strength |
Gouda Vuurvast CURON 170 Dense Refractory Castable Description: A general purpose castable with a wide range of applications for high temperatures. The low Fe2O3 content makes this castable suitable for use under reducing conditions.Remarks: These v.. |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 1300 °C |
7250 - 8700 psi @Temperature 2370 °F |
Cold Crushing Strength |
Gouda Vuurvast CURON 170 Dense Refractory Castable Description: A general purpose castable with a wide range of applications for high temperatures. The low Fe2O3 content makes this castable suitable for use under reducing conditions.Remarks: These v.. |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 100 °C |
7250 - 8700 psi @Temperature 212 °F |
Cold Crushing Strength |
Gouda Vuurvast CURON 170 GM Dense Refractory Castable Description: A general purpose gunning castable with a wide range of applications for high temperatures. The low Fe2O3 content makes this castable suitable for use under reducing conditions.Remarks:.. |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 1300 °C |
7250 - 8700 psi @Temperature 2370 °F |
Cold Crushing Strength |
Gouda Vuurvast CURON 170 GM Dense Refractory Castable Description: A general purpose gunning castable with a wide range of applications for high temperatures. The low Fe2O3 content makes this castable suitable for use under reducing conditions.Remarks:.. |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 100 °C |
7250 - 8700 psi @Temperature 212 °F |
Cold Crushing Strength |
Gouda Vuurvast FLUCON 140 Dense Self Flowing Refractory Castable Description: Flucon 140 is a self flowing low cement castable, based on a high quality chamotte grog.Remarks: These values apply to cast products.Information provided by Gouda Vuurvast. |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 100 °C |
7250 - 8700 psi @Temperature 212 °F |
Cold Crushing Strength |
Gouda Vuurvast CURON 145 Dense Refractory Castable Description: Because of the use of pure raw materials, Curon 145 has a low Fe2O3 content. Therefore this castable is widely used in reducing atmospheres.Remarks: These values apply to cast products... |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 100 °C |
7250 - 8700 psi @Temperature 212 °F |
Cold Crushing Strength |
Gouda Vuurvast CURON 150 Dense Refractory Castable Description: This bauxite based castable has a very good thermal shock resistance and is therefore well suited for burner blocks.Remarks: These values apply to cast products. Also available in gunni.. |
|||
Compressive Strength | 50.0 - 60.0 MPa @Temperature 100 °C |
7250 - 8700 psi @Temperature 212 °F |
Cold Crushing Strength |
Gouda Vuurvast CURON 100 C Dense Refractory Castable Description: Curon 100 C can be applied up to 1000°C, under normal operating conditions and is especially applied in the bottom of electrolytic cells in the aluminum industry.Remarks: These values .. |