Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 1030 MPa @Temperature 650 °C |
149000 psi @Temperature 1200 °F |
Precipitation Hardened prior to test |
Special Metals INCONEL® Alloy 751 A nickel-chromium alloy similar to INCONEL ALLOY X-750 but with increased aluminum content for greater precipitation hardening. INCONEL alloy 751 was designed for use as exhaust valves in internal-.. |
|||
Tensile Strength, Ultimate | 1030 MPa @Temperature 650 °C |
149000 psi @Temperature 1200 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 105 A precipitation-hardenable nickel-cobalt-chromium alloy with an addition of molybdenum for solid-solution strengthening. The relatively high aluminum content enhances both strength (through greater.. |
|||
Tensile Strength, Ultimate | 1030 MPa @Temperature 650 °C |
149000 psi @Temperature 1200 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 80A A nickel-chromium alloy similar to NIMONIC alloy 75 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good corrosion and oxidation resistance and high tensile a.. |
|||
Tensile Strength, Ultimate | 1030 MPa @Temperature 550 °C |
149000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 90 A precipitation-hardenable nickel-chromium-cobalt alloy having high stress-rupture strength and creep resistance at temperatures to about 1700°F (920°C). The alloy also has good resistance to.. |
|||
Tensile Strength, Ultimate | 1030 MPa @Temperature 550 °C |
149000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 901 A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at .. |