Polymer Property : Tensile Strength, Ultimate = 130000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	898 MPa @Thickness 1.45 mm	130000 psi @Thickness 0.0571 in
Haynes HastelloyÂ® S alloy, flat products, solution heat-treated at 649Â°C (1200Â°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	899 MPa @Thickness 12.7 mm, Temperature 25.0 Â°C	130000 psi @Thickness 0.500 in, Temperature 77.0 Â°F	As Welded, Base/Base Fracture
Haynes 282Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Ultimate	895 MPa @Temperature 25.0 Â°C	130000 psi @Temperature 77.0 Â°F	AMS 5879
Haynes 625SQÂ® Nickel Alloy Sheet Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200Â°F (649Â..
Tensile Strength, Ultimate	896 MPa @Thickness <=38.1 mm	130000 psi @Thickness <=1.50 in
Crucible Steel Aquamet® 19 Stainless Steel AQUAMET 19 is a modified Type 304 stainless steel that is fully austenitic and non-magnetic. Strengthened by adding nitrogen to the melt, it has better corrosion resistance than Type 304 stainless. ..
Tensile Strength, Ultimate	896 MPa @Temperature 23.0 °C	130000 psi @Temperature 73.4 °F
ATI Wah Chang TI-3Al-2.5V Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an..