Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	756 MPa @Thickness 9.50 - 25.4 mm, Temperature 316 Â°C	110000 psi @Thickness 0.374 - 1.00 in, Temperature 601 Â°F
Haynes HastelloyÂ® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	758 MPa @Thickness 12.7 mm	110000 psi @Thickness 0.500 in
Haynes HastelloyÂ® C-2000Â® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	756 MPa @Thickness 12.7 mm, Temperature 149 Â°C	110000 psi @Thickness 0.500 in, Temperature 300 Â°F
Haynes HastelloyÂ® Hybrid-BC1Â® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate HASTELLOYÂ® HYBRID-BC1Â® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate	760 MPa @Temperature 23.0 Â°C	110000 psi @Temperature 73.4 Â°F
Special Metals INCONELÂ® Alloy 601 A nickel-chromium alloy with an addition of aluminum for outstanding resistance to oxidation and other forms of high-temperature corrosion. It also has high mechanical properties at elevated temper..
Tensile Strength, Ultimate	760 MPa @Temperature 650 Â°C	110000 psi @Temperature 1200 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 263 A precipitation-hardenable nickel-chromium-cobalt alloy with an addition of molybdenum for solid-solution strengthening. It has high strength and corrosion resistance along with good formability an..
Tensile Strength, Ultimate	756 MPa @Thickness 12.7 mm, Temperature 149 °C	110000 psi @Thickness 0.500 in, Temperature 300 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..
Tensile Strength, Ultimate	758 MPa @Diameter 25.4 mm, Temperature 25.0 °C	110000 psi @Diameter 1.00 in, Temperature 77.0 °F
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..