Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 265 MPa | 38400 psi | 1.3 mm/min; ASTM D790 |
Ovation Polymers Opnyl OP66GF50 Nylon 66 Nylon 66-Glass reinforced(50%), high tensile strength, stiffness and HDT.Information provided by Ovation Polymers |
|||
Flexural Yield Strength | 265 MPa | 38400 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP QF00A PA 6/10 (Europe-Africa-Middle East) LNP* Thermocomp* QF00A is a compound based on Nylon 6/10 resin containing Glass Fiber. |
|||
Flexural Yield Strength | 265 MPa | 38400 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp RF007S PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RF007S is a compound based on PA 66 resin containing Glass Fiber . Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regi.. |
|||
Flexural Yield Strength | 265 MPa | 38400 psi | ASTM D790 |
PlastxWorld Veroplas PB3500 Nylon 66 general purpose, 50% glass filled injection molding gradeInformation provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 265 MPa | 38400 psi | ASTM D790 |
Cheng Yu Plastic N6G30 Nylon 6, 30% Glass Filled |
|||
Flexural Yield Strength | 265 MPa | 38400 psi | 2 mm/min; ISO 178 |
Eurostar Staramide RF007S PA66, 35% Glass Fiber Filled, Injection Molded Staramide RF007S is a 35% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Yield Strength | 265 MPa | 38400 psi | ASTM Data |
BASF Capron® HPN 9233G HS BK-102 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9233G HS BK-102 is a heat stabilized, pigmented black, 33% glass reinforced nylon 6 injection molding grade resin in the High Productivity Nylon Series developed for improved cycle times .. |
|||
Flexural Yield Strength | 265 MPa | 38400 psi | ISO 178 |
Solvay Specialty Polymers Ryton® R-4-220NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-220NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound formulated for enhanced hydrolytic stability in applications re.. |