Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 235 MPa | 34100 psi | ASTM Data |
BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a.. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | ASTM Data |
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with.. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | ASTM D790 |
Samyang Tripet® 2550GN45 Polyethylene Terephthalate, 45% Glass Fiber Reinforced, Flame Retardant
(discontinue TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll information.. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | ASTM D790 |
Solvay Specialty Polymers Kadel® E-1130 Polyketone
(discontinued **) High performance proprietary semi-crystalline polymer based resins with exceptional solvent resistance and high temperature performance. They provide strength and stiffness, plus superior chemical r.. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | DIN 53 452 |
Albis Plastics Tedur® L V 9300-1 PPS, 40% Glass Fiber/Glass Bead
(discontinued **) Improved Impact Strength, Low Flash, Low Warpage. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Hollow Articles Under Pressure, Pump HousingsProcessing: Injection Mo.. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | ASTM D790 |
Solvay Specialty Polymers Ryton® BR111BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® BR111BL is a glass and mineral filled polyphenylene sulfide compounds developed to provide a good combination of mechanical strength and electrical proper.. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | |
Idemitsu Kosan Xarec® N WA 5030 SPS, 30% Glass Filled |
|||
Flexural Yield Strength | 235 MPa @Thickness 3.20 mm |
34100 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical LUCON PO6062 mPPO+CNT+CF+GF Description: Injection Molding, mPPO+CNT+CF+GF, High Strength, Heat StabilityApplication: ATM parts, LCD Cell TrayCAS No. 35134-01-4, 25038-54-4, 65997-17-3, 7440-44-0 and 7782-42-5Information provi.. |
|||
Flexural Yield Strength | 235 MPa @Thickness 3.20 mm |
34100 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
LG Chemical LUMID EG2309B(W) PA66+GF30%, Chemical Resistance(CaCl2, Ethylene Glycol) Feature: Injection Molding, PA66+GF30%, Chemical Resistance(CaCl2, Ethylene Glycol)Application: Radiator Tank, Intercooler TankCAS No. 32131-17-2, 65997-17-3 and 9010-79-9Information provided by LG .. |
|||
Flexural Yield Strength | 235 MPa @Thickness 3.20 mm |
34100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID HI2302A(W) PA6+GF30%, High Impact Feature: Injection Molding, PA6+GF30%, High ImpactApplication: Automotive PartsCAS No. 25038-54-4, 9010-79-1 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | DIN 53455; ASTM D790 |
Kolon KOPET® KP133G45 FR-PET Resin KOPET® is the FR-PET which realizes the good properties and surface of injection molding with good mold process of short cooling time in low molding temperature.Good mold release, good surface of.. |
|||
Flexural Yield Strength | 235 MPa @Thickness 3.20 mm |
34100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical Lupox® SG5500 PBT+PET+GF50% Description: Injection Molding, PBT+PET+GF50%, Good Surface, High StiffnessApplication: E&E, Automotive (Switch)CAS No. 65997-17-3, 24968-12-5 and 25038-59-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EF006 is a compound based on Polyetherimide resin containing Glass Fiber. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | Flexural elongation is 1.5%; ASTM D790 |
Toyobo TS201 PPS, Glass Fiber/Mineral Reinforced Key Feature: Standard high stiffness - used for metal replacementHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology devel.. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | ASTM D790 |
E-Polymers Tekaster® F615G30 , 30% Glass Fiber Reinforced PET 30% Glass Fiber reinforced, High strength, Information provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 235 MPa | 34100 psi | ASTM Data |
BASF Capron® SEG6 H1 BK-122 30% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron SEG6 H1 BK-122 is a black pigmented, 30% glass reinforced nylon 6 injection molding compound. This material is currently under development as XA-2678. It exhibits exceptional surface aesthet.. |