Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 154 MPa | 22300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM UH1006M TPI Blend High heat amorphous TPI Blend, Chemical Resistant |
|||
Flexural Yield Strength | 154 MPa | 22300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical Resistant |
|||
Flexural Yield Strength | 154 MPa | 22300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical Resistant |
|||
Flexural Yield Strength | 154 MPa | 22300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® 6370 PBT+PC 30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility. |
|||
Flexural Yield Strength | 154 MPa | 22300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 451E PBT (Europe-Africa-Middle East) VALOX 451E is 20% glass reinforced, flame retardant PBT injection moulding resin. |
|||
Flexural Yield Strength | 154 MPa | 22300 psi | (102 mm Span) 3mm/min; ASTM D790 |
LNP ULTEM® SMU5832 Polyetherimide, 30% CarbonGlassMineral Reinforced
(discontinued **) ESD characteristics for ultra high-heat applications. Will be UC3010.Features: High Heat ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Compan.. |