Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 7.00 - 140 MPa | 1020 - 20300 psi | Average value: 74.9 MPa Grade Count:39 |
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Flexural Yield Strength | 11.0 - 140 MPa | 1600 - 20300 psi | Average value: 93.6 MPa Grade Count:197 |
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Flexural Yield Strength | 29.9922 - 140 MPa @Temperature -40.0 - 90.0 °C |
4350.01 - 20300 psi @Temperature -40.0 - 194 °F |
Average value: 71.0 MPa Grade Count:4 |
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Flexural Yield Strength | 38.0 - 140 MPa @Temperature -40.0 - 80.0 °C |
5510 - 20300 psi @Temperature -40.0 - 176 °F |
Average value: 86.8 MPa Grade Count:2 |
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum .. |
|||
Flexural Yield Strength | 70.0 - 140 MPa | 10200 - 20300 psi | Average value: 101 MPa Grade Count:22 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |
|||
Flexural Yield Strength | 134 - 140 MPa @Temperature 80.0 - 80.0 °C |
19400 - 20300 psi @Temperature 176 - 176 °F |
Average value: 137 MPa Grade Count:4 |
Overview of materials for Polypropylene with 60% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are i.. |