Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ASTM D882 |
Honeywell Aegisâ„¢ H155ZP Nylon 6 Extrusion Grade Homopolymer Film Description: Aegis H155ZP is a high viscosity, nylon 6 film extrusion grade homopolymer for cast or blown film. It conforms to Food and Drugs Administration requirements of 21 CFR 177.1500 as well a.. |
|||
Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ISO 527-3 |
Borealis Borstar® FB1460 HDPE for Film Borstar FB1460 is a high-density polyethylene film grade, which combines superior physical properties with excellent processability. Due to the high density, the material properties are best utiliz.. |
|||
Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ASTM D882 |
ExxonMobil Exceed™ 1023CA Metallocene Polyethylene Resin (European Grade) Product Description: Exceed 1023CA is a metallocene ethylene-hexene copolymers. The slightly higher stiffness of Exceed 1023CA makes it easier to process on certain filling machinery, whilst still k.. |
|||
Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ISO 527-3 |
EMS-Grivory Grivory® BM 17 PA* Product description: Grilon BM 17 natural is a medium viscosity multi-polyamide with a low melting point. Grilon BM 17 natural has the following features: High flexibility and toughnessVery good ori.. |
|||
Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ISO 527-3 |
EMS-Grivory Grivory® CA 6 E PA* Product description: Grilon CA 6 E is a non-extracted copolyamide with a low melting point. Grilon CA 6 E characterizes itself through the following properties Very high flexibility and toughnessVer.. |
|||
Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ASTM D882 |
Braskem Flexus® 9200 Blown Film Extrusion Polyethylene Description: Flexus 9200 is a LLDPE hexene copolymer produced through metallocene catalyst which presents excellent impact and puncture strength, beyond a differential sealing performance comparing .. |
|||
Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ASTM D882 |
Ashley Polymers Ashlene® 850 Nylon 6 This is an extrusion grade Nylon 6 resin suitable for both coextrusion and blown film applications. It has excellent melt stability and very high melt strength. It also has excellent grease resist.. |
|||
Film Tensile Strength at Break, TD | 60.0 - 100 MPa | 8700 - 14500 psi | Average value: 80.0 MPa Grade Count:5 |
Overview of materials for Nylon 6, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Extruded". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ISO 527-3 |
EMS-Grivory Grivory® BM 20 SBG PA* Product description: Grilon BM 20 SBG is a lactam free multipolyamide. Grilon BM 20 SBG has the following features: Lactam freeGood transparency and glossGood flexibility and toughnessVery good ther.. |