Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T FGH 196 Hexene Copolymer Linear Low Density Polyethylene Clearflex H&T FGH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films obtained from Clearflex H&T FGH .. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 20 F Butene Copolymer Linear Low Density Polyethylene Flexirene FG 20 F is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Main Applications: Flexirene FG 20 F is recommended for the .. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 23 I Butene Copolymer Linear Low Density Polyethylene Flexirene FG 23 I is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Flexirene FG 23 I represents the version of Flexirene FG 20 I.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
NOVA Chemicals Novapol® TD-9022-C Superhexene LLDPE Puncture value is 60 J/mm. Additive Package: Antiblock.Applications: industrial liners, heavy duty packaging.Film properties are typical of 25 µm blown film extruded at a blow-up ratio of 2.5:1, b.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
NOVA Chemicals Novapol® TD-9022-D Super Hexene Film Resin Excellent dart impact, High strength, High toughnessApplications: Retail trash bagsAdditives: Process stabilizer, Slip/antiblockFilm properties are typical of blown film extruded at a blowup ratio o.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® ESD 1100
(discontinued **) PRE-ELEC ESD 1100 is a static dissipative thermoplastic compound based on PETG. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 1100 has been developed for the e.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 20 I Butene Copolymer Linear Low Density Polyethylene Flexirene FG 20 I is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Main Applications: Flexirene FG 20 I is recommended for the .. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Polimeri Europa Flexirene® FG 23 F Butene Copolymer Linear Low Density Polyethylene Flexirene FG 23 F is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Flexirene FG 23 F represents the version of Flexirene FG 20 F.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Chevron Phillips 6109BK LLDPE Blown Film Resin, Butene Copolymer
(discontinued **) Resin Type: Butene Copolymer, Medium Slip, High Antiblock Version of 6109Characteristics: Good Stiffness at Thin Gauges, Good Drawdown, Low COF, Can be used straight or blended with LDPE or HDPE. S.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Chevron Phillips 6109CL LLDPE Blown Film Resin, Butene Copolymer
(discontinued **) Resin Type: Butene Copolymer, High Slip, Very High Antiblock Version of 6109Characteristics: Good Stiffness at Thin Gauges, Good Drawdown, Low COF, Can be used straight or blended with LDPE or HDPE... |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Chevron Phillips 6109DK LLDPE Blown Film Resin, Butene Copolymer
(discontinued **) Resin Type: Butene Copolymer, High Antiblock, Process Aid Version of 6109Characteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or blended with LDPE or HDPEApplications.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Reliance Industries Reclair O19010 Polyethylene Blow film Linear Low Density Polyethylene grade. Reclair O19010 is octene comonomer based, with optimum levels of antioxidants, antiblocking agents, slip additives, and polymer processing aids. Th.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882-02 |
Ipiranga Petrochem LB 0117 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Iran Petrochemical (PCC) 12XF6 Linear Low Density Polyethylene 12XF6 is a high performance LLDPE (HP-LLDPE) blown film grade for high film strength applications.Information provided by Iran Petrochemical Commercial Co. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Iran Petrochemical (PCC) LL 18XF5 N Linear Low Density Polyethylene LL 18XF5 N is a terpolymer of ethylene, propylene and butene-1 for high film strength applications, especially heavy duty shipping sacks, ice bags, frozen food bags, potato bags, and agriculture fil.. |
|||
Film Tensile Strength at Break, TD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
Borealis Borclear™ RD738CF Propylene Alpha Olefin Copolymer for Cast Film Borclear RD738CF is a slip and antiblock formulation propylene alpha olefin copolymer resin. It is suitable for the manufacturing of unoriented film on chill roll process.Borclear RD738CF is suitabl.. |
|||
Film Tensile Strength at Break, TD | 35.0 - 55.0 MPa | 5080 - 7980 psi | ISO 527-3 |
Borealis Borclear™ RE718CF Propylene Alpha Olefin Copolymer for Metallizable Cast Film Borclear RE718CF is a propylene alpha olefin copolymer resin formulation with antiblocking agent and without Ca-stearate, especially developed for the manufacturing of unoriented cast films for meta.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Borealis Bormed™ RD804CF Polypropylene Random Copolymer Bormed™ RD804CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications Bormed™ RD804CF is recommended for packaging for med.. |
|||
Film Tensile Strength at Break, TD | 35.0 - 45.0 MPa | 5080 - 6530 psi | ISO 527-3 |
Borealis Bormed™ TD109CF Polypropylene Copolymer Bormed™ TD109CF is a propylene alpha olefin copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: lamination films, food.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Borealis Borstar® FB4250T LLDPE for Blown Film Borstar FB4250 is well suited for a wide range of film applications due to its properties. The well balanced mechanical properties will improve the functionality of the films or allow for material .. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Total EVA 1005 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1005 VN 4 is made by a high pressure tubular process. Grade for flexible films with high transparency and good mechanical properties. Contains an antioxidant.Application examples: High strengt.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ISO 527-3 |
Total PPH 4026 Polypropylene Homopolymer, Film Polypropylene PPH 4026 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance.Polypropylene PPH 4026 is in.. |
|||
Film Tensile Strength at Break, TD | >= 35.0 MPa | >= 5080 psi | 35 N/10mm |
Dr. D. Mueller Flexiso® DMD FI 14010 00100 Polyester Electrical Insulation Structure: Flexiso® DMD, FI 14010 00100 is a flexible three layer material, consisting of a layer of polyester film, of which both sides have a layer of polyester fleece fabric and is coated with .. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | |
Dow DOWLEX™ 2070D Linear Low Density Polyethylene, Blown Film Grade DOWLEX® 2070D Polyethylene resin is a fully formulated linear low density polyethylene resin offering high strength and low gel properties for blown film food packaging applications. DOWLEX 2070D r.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
DuPont™ Surlyn® 1901 Sodium Ionomer Resin for Blown and Cast Film Surlyn® 1901 is a sodium ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultr.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Braskem LL 118/21 LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Automatic packaging (FFS); "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
NOVA Chemicals Novapol® TF-0242-E Hexene LLDPE Film Resin
(discontinued **) Excellent stiffness and glossApplications: Diaper back sheet, BlendingFilm properties are typical of film extruded at 270°C.Information provided by NOVA Chemicals. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Chevron Phillips 6109L LLDPE Blown Film Resin, Butene Copolymer
(discontinued **) Resin Type: Butene Copolymer, Very High Antiblock Version of 6109Characteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or blended with LDPE or HDPEApplications:Industr.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Chevron Phillips 6109 LLDPE Blown Film Resin, Butene Copolymer
(discontinued **) Resin Type: Butene CopolymerCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Can be used straight or blended with LDPE or HDPEApplications:Industrial Liners, Stretch Wrap, Garment Bags.. |
|||
Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
Chevron Phillips 6109M LLDPE Blown Film Resin, Butene Copolymer
(discontinued **) Resin Type: Butene Copolymer, High Slip, Very High Antiblock Version of 6109Characteristics: Good Stiffness at Thin Gauges, Good Drawdown, Low COF, Can be used straight or blended with LDPE or HDPE... |