Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ISO 527-3 |
Polimeri Europa Clearflex® CL 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex CL 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CL 106 are characterized by h.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |
SABIC 218 Series Linear Low Density Polyethylene for Blown Film Product Description: 218 series resins are Linear Low Density Polyethylene grades suitable for general purpose packaging. They are easy to process giving good tensile properties, impact strength a.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ISO 527-3 |
Polimeri Europa Greenflex® FF 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FF 45 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FF 45 show high toughness.Main Applications: Greenflex FF 45 is recommended for.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |
Petroquimica Triunfo Trilene® TS 8056 LLDPE-C8 and LDPE Blend The Trilene TS 8056 product is a blend with a high ratio of linear low-density polyethylene - octene comonomer (LLDPE-C8) with low-density polyethylene (LDPE) with elevated processability, ensuring .. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |
Petroquimica Triunfo Trilene® TS 8057 LLDPE-C4 and LDPE Blend The Trilene® TS 8057 product is a blend with a high ratio of linear low-density polyethylene - butene copolymer (LLDPE) with low-density polyethylene (LDPE) providing elevated processability and en.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
ExxonMobil Escorene® LD 767.MJ Cast and Compounding Film Resin
(discontinued **) Escorene Ultra LD 767.MJ is a low gel 29.5% vinyl acetate copolymer designed for film and compounding applications.Information provided by ExxonMobil Chemical |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |
LyondellBasell Montell 16502F3 Butene LLDPE Key Features: butene LLDPE resins for film extrusion applications, easy processing, low gels, good strength, no slip, no antiblockApplications: can liners and trash bags, blends, thin filmsMeets FDA.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |
LyondellBasell Montell 16502F7 Butene LLDPE Key Features: butene LLDPE resins for film extrusion applications, easy processing, low gels, good strength, low slip, medium antiblockApplications: can liners and trash bags, blends, thin filmsMeet.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |
LyondellBasell Montell 16502F8 Butene LLDPE Key Features: butene LLDPE resins for film extrusion applications, easy processing, low gels, good strength, medium slip, high antiblockApplications: can liners and trash bags, blends, thin filmsMee.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
LyondellBasell Petrothene® GA601031 Linear Low Density Polyethylene ApplicationsPETROTHENE® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
LyondellBasell Petrothene® GA601032 Linear Low Density Polyethylene ApplicationsPETROTHENE® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
LyondellBasell Petrothene® GA601033 Linear Low Density Polyethylene ApplicationsPETROTHENE® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
LyondellBasell Petrothene® NA285003 Medium Density Polyethylene ApplicationsPETROTHENE NA 285-003 is a medium density polyethylene resin for blown or cast film extrusion. Typical applications include overwrap film. This product exhibits good film optics and hi.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
LyondellBasell Petrothene® GA601030 Linear Low Density Polyethylene ApplicationsPETROTHENE® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
LyondellBasell Petrothene® LP540200 High Density Polyethylene ApplicationsPETROTHENE LP 5402-00 is a copolymer resin designed for blown film applications. This resin offers high stiffness, excellent appearance and bubble stability and good draw-down. LP 5402-0.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | |
UBE 1022FDX23 Nylon 6 Homopolymer Film Specialties: High slip typeProcessing: Water cooling processTypical applications: small pouch & generalInformation provided by UBE. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
ExxonMobil Escorene™ UL 00112 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00112 is a fractional MI copolymer of ethylene and vinyl acetate.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: No Applica.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | Calculated from mfr's report of 78 N/cm per ASTM D828 and the typical thickness |
DuPont™ Nomex® 418 Paper, 10 mil Nominal Thickness Nomex® Type 418 is designed for high-voltage applications such as motor conductor and coil wrap, transformer ground and layer insulation. It can be readily impregnated with varnishes. This calen.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | |
Dow DOWLEX™ 2101 Linear Low Density Polyethylene, Blown Film Grade DOWLEX® 2101 Polyethylene resin, a general purpose blown film extrusion resin, is an excellent choice for high speed, thin gauge film applications. It contains medium levels of both slip additive a.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |
Braskem LL 218/21 LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Automatic packaging (FFS); "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem |
|||
Film Tensile Strength at Break, TD | 29.0 - 303 MPa | 4210 - 44000 psi | Average value: 128 MPa Grade Count:21 |
Overview of materials for Nylon 6, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Film Grade". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
ExxonMobil Escorene™ FL 00112 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00112 is a copolymer of ethylene and vinyl acetate offering low gel. Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: No App.. |