Polymer Property : Tensile Strength, Yield = 92100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Yield	635 MPa @Strain 0.200 %	92100 psi @Strain 0.200 %
Haynes 214Â® alloy, 30% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	635 MPa @Strain 0.200 %	92100 psi @Strain 0.200 %
Haynes 230Â® alloy, 10% cold reduction, 1066Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield	635 MPa @Strain 0.200 %, Temperature 760 Â°C	92100 psi @Strain 0.200 %, Temperature 1400 Â°F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595Â°C (1100Â°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	635 MPa @Strain 0.200 %	92100 psi @Strain 0.200 %
Haynes 25 alloy, room temperature sheet after 1000 hours of 650Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	635 MPa @Strain 0.200 %	92100 psi @Strain 0.200 %
Haynes 263Â® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle..
Tensile Strength, Yield	635 MPa	92100 psi
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 30% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi..