Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 205 MPa | 29700 psi | ISO 527, ASTM D638 |
Nilit Nilamid A3 H G8 40% Glass Reinforced PA66 Description: Nilamid A3 H G8 is a high strength material, that is used for structural applications. It is easy to mould, and shows outstanding stiffness and creep resistance, even at elevated temper.. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 175 Cast UNS C95400 Aluminum Bronze Versatile alloy with high strength, good ductility, unusual toughness, plus exceptional wear resistance. Aluminum Bronze heat treated to higher mechanical properties where necessary.Information prov.. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 20M Cast UNS J94650 Super Austenitic Stainless Steel Corrosion resistance approaching nickel alloys, especially in chloride service.Applications: Process piping exposed to flue gas and solutions.Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 304 Cast J92600 Austenitic Stainless Steel "300" series, general corrosion resistant alloyApplications: Nuclear, chemical and food processing. Valve and pump trim.Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 309 Cast UNS J93400 Austenitic Stainless Steel "300" series, general corrosion resistant alloyApplications: Nuclear, chemical and food processing. Valve and pump trim.Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 316 Cast UNS J92900 Austenitic Stainless Steel "300" series, general corrosion resistant alloyApplications: Nuclear, chemical and food processing. Valve and pump trim.Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 316L Cast UNS J92800 Austenitic Stainless Steel "300" series, general corrosion resistant alloyApplications: Nuclear, chemical and food processing. Valve and pump trim.Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 347 Cast UNS J92710 Austenitic Stainless Steel "300" series, general corrosion resistant alloyApplications: Nuclear, chemical and food processing. Valve and pump trim.Information provided by MetalTek |
|||
Tensile Strength, Yield | 205 MPa @Strain 0.200 %, Temperature 980 °C |
29700 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 302 Cast CF16Fa Austenitic Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
MetalTek MTEK 304L Cast UNS J92500 Austenitic Stainless Steel "300" series, general corrosion resistant alloyApplications: Nuclear, chemical and food processing. Valve and pump trim.Information provided by MetalTek |
|||
Tensile Strength, Yield | 205 MPa @Strain 0.200 %, Temperature 980 °C |
29700 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 205 MPa @Strain 0.200 %, Temperature 425 °C |
29700 psi @Strain 0.200 %, Temperature 797 °F |
|
Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 205 MPa @Strain 0.200 %, Temperature 870 °C |
29700 psi @Strain 0.200 %, Temperature 1600 °F |
|
Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 205 MPa | 29700 psi | ASTM D638 |
Solvay TECHNYL® 2412GHF8 PA66, 40% glass fiber, DRY Description: Polyamid 66, reinforced with 40% of glass fiber, heat stabilized for injection moldingAvailable in: Asia PacificProduct Applications: TECHNYL® 2412GHF8 is used in all sectors of indu.. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
AK Steel ASTM A 570, Grade 30 Hot Rolled Carbon Steel, Structural Quality (SQ) For gauges up to 0.229", ASTM A 570 must be specified, gauges >0.230", ASTM A 907 must be used. Items 0.180 to 0.230" gauge which are >48" wide may be ordered to either A 570 or A 907.Information p.. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
AK Steel ASTM A 907, Grade 30 Hot Rolled Carbon Steel, Structural Quality (SQ) For gauges up to 0.229", ASTM A 570 must be specified, gauges >0.230", ASTM A 907 must be used. Items 0.180 to 0.230" gauge which are >48" wide may be ordered to either A 570 or A 907.Information p.. |
|||
Tensile Strength, Yield | 205 MPa | 29700 psi | 50mm/min; ISO 527 |
BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Dry) Ultramid B3G8 BK00564 is a 40% glass filled, pigmented black, injection molding PA6 grade. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | ASTM A240 |
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Molybdenum 317L (UNS S31703) Allegheny Ludlum's 317L™ is molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless s.. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | ASTM A240 |
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Molybdenum 317LX™ (UNS S31725) Allegheny Ludlum's 317LX™ is molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless .. |
|||
Tensile Strength, Yield | >= 205 MPa @Strain 0.200 % |
>= 29700 psi @Strain 0.200 % |
Annealed; Min required by ASTM A 240 and ASME SA-240 |
ATI Allegheny Ludlum Type 317 Stainless Steel, UNS S31700 This is a molybdenum-bearing austenitic stainless steels which is more resistant to general corrosion and pitting/crevice corrosion than the conventional chromium-nickel austenitic stainless steels .. |
|||
Tensile Strength, Yield | 205 MPa @Strain 0.200 % |
29700 psi @Strain 0.200 % |
|
ATI Allvac® Nickelvac® 304 L UNS S30403 Specialty Steel Widely used stainless steel for corrosion resistant application. CPI HX and vessels, tubing, wire, medical and dental devices.Property values are for samples in the metallurgical condition: 1900°F .. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
AK Steel ASTM A 1011, Grade 30 Hot Rolled Carbon Steel, Structural Steel (SS) Information provided by AK Steel |
|||
Tensile Strength, Yield | >= 205 MPa @Strain 0.200 % |
>= 29700 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Stainless Steel Type 301, annealed (UNS S30100) Allegheny Ludlum Type 301 is a high strength grade of steel available in six conditions or tempers, its resistance to atmosphere corrosion and its bright, attractive surface make it an excellent cho.. |
|||
Tensile Strength, Yield | >= 205 MPa @Strain 0.200 % |
>= 29700 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Stainless Steel Type 348 (UNS S34800) AL 348 is a stabilized stainless steel which offers excellent resistance to intergranular corrosion following exposure to temperatures in the chromium carbide precipitation range from 800° to 1500°.. |
|||
Tensile Strength, Yield | >= 205 MPa @Strain 0.200 % |
>= 29700 psi @Strain 0.200 % |
Annealed; Min required by ASTM A 240 and ASME SA-240 |
ATI Allegheny Ludlum Type 316 Stainless Steel, UNS S31600 This is a molybdenum-bearing austenitic stainless steels which is more resistant to general corrosion and pitting/crevice corrosion than the conventional chromium-nickel austenitic stainless steels .. |
|||
Tensile Strength, Yield | >= 205 MPa | >= 29700 psi | |
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, Annealed (UNS S30400) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
Tensile Strength, Yield | >= 205 MPa @Strain 0.200 % |
>= 29700 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Stainless Steel Type 321 (UNS S32100) AL 321 is a stabilized stainless steel which offers excellent resistance to intergranular corrosion following exposure to temperatures in the chromium carbide precipitation range from 800° to 1500°.. |
|||
Tensile Strength, Yield | >= 205 MPa @Strain 0.200 % |
>= 29700 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Stainless Steel Type 347 (UNS S34700) AL 347 is a stabilized stainless steel which offers excellent resistance to intergranular corrosion following exposure to temperatures in the chromium carbide precipitation range from 800° to 1500°.. |