Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 8.80 MPa | 1280 psi | -20% change after 72 hours @ 250°C; ASTM D412 |
Precision Polymer Engineering V90D Fluoroelastomer Compound Fluoroelastomer Rubber, 86-93 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Meets Aerospace Specifications DTD5612A and DTD5543B Grade 90. ASTM designation = FKM. ISO designatio.. |
|||
Tensile Strength, Yield | 8.80 MPa | 1280 psi | -20% change after 72 hours @ 250°C; ASTM D412 |
Precision Polymer Engineering V90H Fluoroelastomer Compound Fluoroelastomer Rubber, 85-95 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Formulated using only those ingredients determined by the United States Federal Food and Drug Administ.. |
|||
Tensile Strength, Yield | 8.80 MPa | 1280 psi | ASTM D638 |
NOVA Chemicals Novapol® LA-0219-A LDPE Foam Resin Features: Good heat sealing latitudeModerate toughnessEasy processability Applications: Industrial packagingLinersBlends with LLDPEFoam ArticlesInformation provided by Nova Chemicals |
|||
Tensile Strength, Yield | 8.80 MPa | 1280 psi | ASTM D638 |
NOVA Chemicals Novapol® LA-0219-AM LDPE Foam Resin Good heat sealing latitude, Moderate toughness, Easy processabilityApplications: Industrial packaging, Liners, Blends with LLDPE, Foam articlesAdditives: Base resinFilm properties are typical of blo.. |
|||
Tensile Strength, Yield | 8.80 MPa | 1280 psi | ASTM D638 |
NOVA Chemicals Novapol® LA-0218-AF LDPE Foam Resin
(discontinued **) Good heat sealing latitude, Moderate toughness, Easy processabilityApplications: Specifically designed for foam process, Blends with LLDPEAdditives: Base resinFilm properties are typical of blown fi.. |
|||
Tensile Strength, Yield | 8.80 - 35.0 MPa | 1280 - 5080 psi | Average value: 19.4 MPa Grade Count:34 |
Overview of materials for High Density Polyethylene (HDPE), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Film Grade". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 102-15 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 102-16 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 102-17 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 102-21 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 102-23 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 102-57 Low Density Polyethylene Composite, for Further Radiation Modification Production Method: Composition is produced on the basis of 10204-003 base grade low density polyethylene or first and primary grades. Application: Used for heat and radiation resistant wires and.. |
|||
Tensile Strength, Yield | >= 8.80 MPa | >= 1280 psi | |
Kazanorgsintez 108-225 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 153-15 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 153-21 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 153-23 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | >= 8.80 MPa | >= 1280 psi | |
Kazanorgsintez 158-225 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg.. |
|||
Tensile Strength, Yield | >= 8.80 MPa | >= 1280 psi | |
Kazanorgsintez 158-76 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg.. |
|||
Tensile Strength, Yield | 8.83 MPa | 1280 psi | 200 mm/min; ASTM D638 |
LG Chemical LUTENE LB5000 LDPE Extrusion Coating Description: LUTENE LB5000 is mainly intended for extrusion coating and can be processed at high speed uniform thickness and width. LUTENE LB5000 is also noted for the excellent adhesion to porous a.. |
|||
Tensile Strength, Yield | 8.83 MPa | 1280 psi | 200 mm/min; ASTM D638 |
LG Chemical LUTENE LB7500 LDPE Extrusion Coating Description: LUTENE LB7500 is mainly intended for extrusion coating and can be processed at high speed uniform thickness and width. LUTENE LB7500 is also noted for the excellent adhesion to porous a.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 153-17 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |
|||
Tensile Strength, Yield | 8.83 MPa | 1280 psi | ASTM D638 |
SCG Chemicals EL-Leneâ„¢ LD1630J Low Density Polyethylene Injection Molding Key Characteristics:Good flowability for multicavitiesGood toughness and flexibilityExcellent gloss and transparencyOdorlessSafe for food contactRecommended Applications:HousewaresSmall to large clo.. |
|||
Tensile Strength, Yield | 8.83 MPa | 1280 psi | at 300% elongation; ASTM D412 |
Lubrizol Estane® S180A Thermoplastic Polyurethane Type: Estane® S180A is a Shore 83A, polyester based thermoplastic polyurethane (TPU). FDA approved (21 CFR 177.2600, 177.1680).Uses: Injection Molding, Extrusion.Availability: Americas, Europe, Mi.. |
|||
Tensile Strength, Yield | 8.827 MPa | 1280 psi | 104.6% Retention; Air Over Aged 1008 hrs at 100°C, Perpendicular |
Teknor Apex TEKRON® 4300-D88A Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | 8.83 MPa | 1280 psi | at 300% elongation; ASTM D412 |
Lubrizol Estane® R175A Thermoplastic Polyurethane Type: Estane® R175A is a Shore 75A, plasticized grade thermoplastic polyurethane (TPU).Uses: Injection Molding.Information Provided by The Lubrizol Corporation |
|||
Tensile Strength, Yield | 8.83 MPa | 1280 psi | ASTM D412 |
Teknor Apex TEKRON® 4000-60 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | Cable at 100°C, 10 days; ASTM D638 |
Borealis Casico™ FR4804 Non-Halogen Flame Retardant Compound for Low Voltage Insulation and Jacketing Borstar FR4804 is a natural, thermoplastic polyolefin compound designed for flame retardant low voltage wire insulation and jacketing. As such, FR4804 offers a unique combination of good extrusion p.. |
|||
Tensile Strength, Yield | 8.80 MPa | 1280 psi | |
Dow Primacor® 3150 Ethylene Acrylic Acid (EAA) PRIMACOR® 3150 polymer containing 3% comonomer is an extrusion/ coextrusion coating and laminating for flexible packaging applications. It is designed to provide excellent adhesion to metallic, pap.. |
|||
Tensile Strength, Yield | >= 8.80 MPa | >= 1280 psi | |
Kazanorgsintez 108-76 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg.. |
|||
Tensile Strength, Yield | >= 8.83 MPa | >= 1280 psi | |
Kazanorgsintez 153-16 Composition of Low Density Polyethylene, Crack-Proof Production Method: Composition is achieved on the basis of grades 10204-003, 15303-003, 10703-020 and formulas of additives 15, 16, 17, 18, 19, 20, 21, 22, and 23. Application: Intended for prod.. |