Polymer Property : Tensile Strength, Yield = 122000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	841 MPa @Temperature 21.1 °C	122000 psi @Temperature 70.0 °F	0° Direction, Dry; Vacuum/Oven Cured; ASTM D3039-95
Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T700 12K 2x2 Twill Reinforced Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request...
Tensile Strength, Yield	843 MPa	122000 psi	at Center, Longitudinal
International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure â€“ no pin holes, inclusions or hard spots. 30-3..
Tensile Strength, Yield	843 MPa	122000 psi	at Center, Transverse
International Mold Steel PX5 Pre-Hardened Mold Steel (P20 Type) PX5 is a modified P20, high performance, high precision, mold steel. Unique Characteristics: Exceptionally clean steel with uniform microstructure â€“ no pin holes, inclusions or hard spots. 30-3..
Tensile Strength, Yield	840 MPa @Strain 0.200 %	122000 psi @Strain 0.200 %
Haynes 214Â® alloy, 10% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	840 MPa @Strain 0.200 %	122000 psi @Strain 0.200 %
Haynes 242Â® alloy, after 4000 hours exposure at 650Â°C (1200Â°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Tensile Strength, Yield	841 MPa @Strain 0.200 %, Temperature 260 °C	122000 psi @Strain 0.200 %, Temperature 500 °F
Carpenter Thermo-Span® Fe-Co-Ni Superalloy Data provided by Carpenter Technology Corporation.Thermo-Span® alloy is a precipitation hardenable superalloy which exhibits a low coefficient of thermal expansion over a broad temperature range, h..
Tensile Strength, Yield	841 MPa	122000 psi
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 30% Cold Rolled (UNS S30200) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to ..