Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 820 MPa @Strain 0.200 %, Temperature 650 °C |
119000 psi @Strain 0.200 %, Temperature 1200 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 819 MPa @Strain 0.200 %, Temperature 760 °C |
119000 psi @Strain 0.200 %, Temperature 1400 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Tensile Strength, Yield | 820 MPa @Strain 0.200 % |
119000 psi @Strain 0.200 % |
|
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Yield | 822 MPa | 119000 psi | Tensile Warp, Dry/RT; Pr EN 2561 |
Hexcel® HexFlow® RTM 120/HY 2954 120°C Epoxy System for RTM Two Component System RTM 120/HY2954 is a two component system, developed for the manufacture of high performance Aerospace and Industrial composite parts using the Advanced Resin Transfer Moulding Process. |
|||
Tensile Strength, Yield | 820 MPa @Temperature 24.0 °C |
119000 psi @Temperature 75.2 °F |
Dry |
Hexcel® HexPly® F522 Epoxy Resin, F3C584 Carbon Fabric Hexcel designation: F3C584-42"-F522; Fiber: Toho® G30/500-3KInformation provided by HexCel |
|||
Tensile Strength, Yield | 820 MPa @Temperature 23.0 °C |
119000 psi @Temperature 73.4 °F |
0°, Conditioning: 23°C; ASTM D3039 |
Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, AS4-C Fiber Designation: C193PW, Plain weaveInformation provided by HexCel |
|||
Tensile Strength, Yield | 820.8 MPa | 119000 psi | Warp; EN2597B |
Ensinger TECATEC™ CF60 Polyaryletherketone (PAEK) TECATEC™ CF60 plate is a composite of 60% woven carbon fiber laminated with a polyaryl ether ketone resin (PAEK). It is produced in a proprietary process yielding good fibre and resin integration... |
|||
Tensile Strength, Yield | 821 MPa @Strain 0.200 %, Temperature 177 °C |
119000 psi @Strain 0.200 %, Temperature 351 °F |
|
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
Tensile Strength, Yield | 819 MPa @Treatment Temp. 649 °C, Time 2.88e+7 sec |
119000 psi @Treatment Temp. 1200 °F, Time 8000 hour |
0.2%. Room temp test after thermal exposure |
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |