Polymer Property : Tensile Strength, Yield = 1160 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	8.00 MPa	1160 psi	ISO 527
Polimeri Europa Clearflex® MQ B0 Very Low Density Polyethylene Clearflex MQ B0 is a linear polyethylene, with antioxidants, characterized by a very low density (VLDPE).The resin shows an excellent balance between flexibility and impact resistance.Main Applicati..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering E70V Ethylene Propylene Rubber Peroxide cured, blue-violet Ethylene Propylene Terpolymer, 65-75 °IRHD. Terpolymer of ethylene, propylene and diene monomers. Specially formulated for sealing applications involving high voltage ..
Tensile Strength, Yield	8.00 MPa	1160 psi	-20% change after 70 hours @ 125°C; ASTM D412
Precision Polymer Engineering E70X Ethylene Propylene Rubber Peroxide cured, Ethylene Propylene Rubber, 65-75 °IRHD. Copolymer of ethylene and propylene.Applications: Excellent water and steam resistance with good compression set properties. Superior heat a..
Tensile Strength, Yield	8.00 MPa	1160 psi	-20% change after 70 hours @ 125°C; ASTM D412
Precision Polymer Engineering E90K Ethylene Propylene Rubber General purpose, peroxide cured, Ethylene Propylene Terpolymer, 85-95 °IRHD. Terpolymer of ethylene, propylene and diene monomers. ASTM D2000/SAE J200 line call out M8CA910, A25, B35, C32, EA14, ..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering H50B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 45-55 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. ASTM and ISO designation = GECO.Applications: Excellent resistance t..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering H60B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 55-65 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. To ASTM D2000 line call-out: M3CH608, A25, B14, EO16, EO36, F17. AS..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering J80P Butyl Rubber Phenolic/Resin cured Butyl Rubber, 75-85 IRHD. Isobutylene-Isoprene Rubber.Applications: Butyl is resistant to the same fluids as Ethylene Propylene (EPDM). It has excellent resistance to gas permea..
Tensile Strength, Yield	8.00 MPa	1160 psi	-20% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering N80L Nitrile Rubber Nitrile Butadiene Rubber, 75-85 °IRHD. Low acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet ASTM D2000 line call-out M6BG814, A14, B14, EO14, EO34, F17.Applications: T..
Tensile Strength, Yield	8.00 MPa	1160 psi	-20% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering Q90Y Polyurethane Rubber Peroxide cured, yellow Polyurethane Rubber, 85-95 °IRHD. Polyester-based urethane. To meet ASTM line call-out M5BG910, B14, EO14, EO34. ASTM & ISO designation = AU.Applications: Excellent abrasio..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering S60B Silicone Rubber Black Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States F..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering S60G Silicone Rubber Green Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States F..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering S60Y Silicone Rubber Yellow Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States ..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering S70A Silicone Rubber Blue Silicone Rubber, 66-75 °IRHD.Complies with the formulation guidelines of the FDA. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent ..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering S70G Silicone Rubber Green Silicone Rubber, 66-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States F..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Precision Polymer Engineering S70T Silicone Rubber Translucent Silicone Rubber, 66-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. ASTM & ISO designation = VMQ.Applications: Excellent heat resistanc..
Tensile Strength, Yield	8.00 MPa	1160 psi	20 in/min, injection molded, type 1 specimen; ASTM D638
Phillips Sumika Marlex® CHP-010 Thermoplastic Polyolefin (discontinued **) Applications: Soft interior trimSoft touch overmoldingInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011.
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D638
Huntsman PE1605 EVA Film Extrusion (discontinued **) 6% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D638
Huntsman PE1651 EVA Film Extrusion (discontinued **) 6.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with outstanding low temperature strength, excellent clarity, and good heat seal.Applications: Film extrusion: ice bags, liqui..
Tensile Strength, Yield	8.00 MPa	1160 psi
LyondellBasell LupolenÂ® V 2920 K Ethylene Vinyl Acetate, lnjection Molding Grade Injection moldingsData was collected by ISO methods and originally provided by BASF. The LupolenÂ® product line is now produced by Basell.
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp FX00617 PE LNP* Lubricomp* FX00617 is a compound based on Polyethylene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Amer..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D638
SPS Guang Zhou POPTREEâ„¢ 6001 Flame-retarded Polyethylene Characteristic: Low density, superior melt flow index, high notched impact strengthApplications: X'mas decorative productInformation Provided by SPS (Guang Zhou) Ltd.
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Teknor Apex APEXÂ® 3211-55 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling..
Tensile Strength, Yield	8.00 MPa	1160 psi	ASTM D412
Vicone High Performance Rubber VicoSil™ KC605Q-OR High Performance Silicone Rubber Information provided by Vicone
Tensile Strength, Yield	8.00 MPa	1160 psi	ISO 527-2
Total LDPE 1700 MN 18 C Low Density Polyethylene - Injection Molding and Compounding LDPE 1700 MN 18 C is a low density polyethylene made by a high pressure autoclave process without antioxidant. Grade for easy flow injection molding of flexible parts, powder production for grindin..
Tensile Strength, Yield	8.00 MPa	1160 psi
Trelleborg B570 Nitrile Rubber Nitrile rubber or acrylonitrile-butadiene rubber is a copolymer of butadiene and acrylonitrile.PropertiesGood general resistance to oils.Good mechanical properties especially tensile strength, flexi..
Tensile Strength, Yield	8.00 MPa	1160 psi
Trelleborg Neoprene® C432 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade..
Tensile Strength, Yield	8.00 MPa	1160 psi
Trelleborg R525 Commercial Natural Rubber Polyisoprene All information provided by Trelleborg
Tensile Strength, Yield	8.00 MPa	1160 psi
Trelleborg S750 Silicone Rubber PropertiesExcellent resistance to heat (dry air), at +200°C continuous and +220°C intermittent.Remains flexible at low temperatures of -70°C.Resistant to ultra-violet light, ozone and weathering...
Tensile Strength, Yield	8.00 MPa @Strain 100 %	1160 psi @Strain 100 %	ISO 527-1/-2
Covestro Desmopan® 445 Polyurethane injection molding gradegrease and oil-resistantgood heat resistancelow compression setApplicationAutomotive engineeringInjection molded engineering partsPreprocessingMax. Water content
Tensile Strength, Yield	8.00 - 9.00 MPa	1160 - 1310 psi	Average value: 8.50 MPa Grade Count:4
Overview of materials for Low Density Polyethylene (LDPE), Masterbatch Grade This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Masterbatch Grade". Each property range of values reported is minimum a..