Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 772 MPa | 112000 psi | |
Meehanite K-325 Austempered Ductile Iron Type K-325 is used for applications such as gears requiring high contact rolling and tooth bending fatigue properties. Type K-325 also possess high fracture toughness impact strength. Excellent fo.. |
|||
Tensile Strength, Yield | 770 MPa | 112000 psi | Typical, 1/2 t |
Industeel SUPERELSO® 690CR Quenched and Tempered High Strength Steel for Leg Components of Jack-up Rigs Superelso® 690 CR (SE 690 CR) is a 690MPa (100ksi) yield strength quenched and tempered steel adapted for jack-up rig legs of offshore drilling platforms. Superelso® 690 CR is manufactured via.. |
|||
Tensile Strength, Yield | 770 MPa @Strain 0.200 %, Temperature 650 °C |
112000 psi @Strain 0.200 %, Temperature 1200 °F |
|
Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
Tensile Strength, Yield | 770 MPa @Strain 0.200 %, Temperature 760 °C |
112000 psi @Strain 0.200 %, Temperature 1400 °F |
|
Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
Tensile Strength, Yield | 770 MPa @Strain 0.200 % |
112000 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
Special Metals NIMONIC® Alloy 105 A precipitation-hardenable nickel-cobalt-chromium alloy with an addition of molybdenum for solid-solution strengthening. The relatively high aluminum content enhances both strength (through greater.. |
|||
Tensile Strength, Yield | 774 MPa @Temperature 175 °C |
112000 psi @Temperature 347 °F |
Material as cured |
Hexcel® HexPly® 922-1/35%/G926 180°C Curing Epoxy Matrix 5H satin/370g/m2 carbon fabric: FVC=60%Information provided by HexCel |
|||
Tensile Strength, Yield | 775 MPa | 112000 psi | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
Tensile Strength, Yield | 773 MPa @Strain 0.200 %, Temperature 649 °C |
112000 psi @Strain 0.200 %, Temperature 1200 °F |
|
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |