Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 70.0 - 75.0 MPa | 10200 - 10900 psi | Type 1B, 50mm/min; ISO 527-1/2:1993 |
Nylacast Oilon Cast Nylon 6, Lubricated (Lubricant Oil Filled) This exceptional oil-loaded nylon features a complex blended oil lubrication system, uniformly distributed throughout the product, that guarantees constant performance over the whole service life. E.. |
|||
Tensile Strength, Yield | 50.0 - 75.0 MPa | 7250 - 10900 psi | Injection; ISO 527 |
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr.. |
|||
Tensile Strength, Yield | 44.1 - 75.0 MPa | 6400 - 10900 psi | Average value: 55.0 MPa Grade Count:12 |
Overview of materials for Acetal Copolymer, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Mineral Filled". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Yield | 49.6 - 75.0 MPa | 7200 - 10900 psi | Average value: 62.8 MPa Grade Count:97 |
Overview of materials for Polycarbonate, UV Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, UV Stabilized". Each property range of values reported is minimum and maximum values of a.. |
|||
Tensile Strength, Yield | 50.0 - 75.0 MPa @Temperature 60.0 - 140 °C |
7250 - 10900 psi @Temperature 140 - 284 °F |
Average value: 63.3 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Tensile Strength, Yield | 2.07 - 75.0 MPa | 300 - 10900 psi | Average value: 27.9 MPa Grade Count:100 |
Overview of materials for Polypropylene, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Flame Retardant". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Yield | 21.0 - 75.0 MPa | 3050 - 10900 psi | Average value: 43.2 MPa Grade Count:39 |
Overview of materials for Polypropylene with 10% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Glass Fiber Filler". Specific grades with glass content between 5% and 14% are in.. |