Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 760 MPa | >= 110000 psi | |
MetalTek IN® 718 UNS N07718 Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 760 MPa | >= 110000 psi | |
MetalTek MTEK 718 Cast UNS N07718 Severe Corrosion and Heat Resistant Alloy Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 760 MPa | >= 110000 psi | |
MetalTek RENE® 77 Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTekWrought Grade RENE® 77 |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 %, Temperature 95.0 °C |
110000 psi @Strain 0.200 %, Temperature 203 °F |
|
Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 %, Temperature 650 °C |
110000 psi @Strain 0.200 %, Temperature 1200 °F |
Precipitation Hardened prior to test |
Special Metals INCONEL® Alloy 751 A nickel-chromium alloy similar to INCONEL ALLOY X-750 but with increased aluminum content for greater precipitation hardening. INCONEL alloy 751 was designed for use as exhaust valves in internal-.. |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 %, Temperature 550 °C |
110000 psi @Strain 0.200 %, Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals INCONEL® Alloy X-750 A nickel-chromium alloy similar to INCONEL alloy 600 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good resistance to corrosion and oxidation along with hig.. |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
Precipitation Hardened |
Special Metals NI-SPAN-C® Alloy 902 A nickel-iron-chromium alloy made precipitation hardenable by additions of aluminum and titanium. The titanium content also helps provide a controllable thermoelastic coefficient, which is the allo.. |
|||
Tensile Strength, Yield | >= 760 MPa @Strain 0.200 % |
>= 110000 psi @Strain 0.200 % |
L and LT Directions |
TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 1.75 - 2.50 in Rod or Thickness; Per ASTM F136) Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
Tensile Strength, Yield | >= 760 MPa @Strain 0.200 % |
>= 110000 psi @Strain 0.200 % |
L, LT and ST Directions |
TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 2.50 - 4.00 in Rod or Thickness; Per ASTM F136) Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
Tensile Strength, Yield | 760 - 830 MPa @Strain 0.200 % |
110000 - 120000 psi @Strain 0.200 % |
|
CLAL-MSX DECLAFOR® 1015 TH2 Wire quenched/Precipitation Heat Treated Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn.. |
|||
Tensile Strength, Yield | 760 MPa | 110000 psi | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
Carpenter Pyromet® CTX-3 Superalloy, Heat Treatment for Brazing Cycles over 982°C Data provided by Carpenter Technology Corporation.Pyromet® alloy CTX-3 is a high strength, precipitation hardenable superalloy which exhibits a low CTE over a broad temperature range. This alloy a.. |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum AL 17-4 High Strength Stainless Steel, UNS S17400 Property data below is typical of annealed samples. Available in plate. For use in fasteners, fittings, military equipment and air frame parts.Information provided by Allegheny Ludlum |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum AL 15-5 High Strength Stainless Steel, UNS S15500 Property data below is typical of annealed samples. Available in plate. For use in fasteners, military equipment and air frame parts.Information provided by Allegheny Ludlum |
|||
Tensile Strength, Yield | 760 MPa @Strain 0.200 % |
110000 psi @Strain 0.200 % |
|
Carpenter BioDur™ CCM® Medical Implant Alloy, Hot Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |