Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 725 MPa | >= 105000 psi | |
MetalTek GTD 222® Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTek |
|||
Tensile Strength, Yield | 725 MPa @Strain 0.200 % |
105000 psi @Strain 0.200 % |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 725 MPa @Strain 0.200 % |
105000 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
Special Metals NIMONIC® Alloy 90 A precipitation-hardenable nickel-chromium-cobalt alloy having high stress-rupture strength and creep resistance at temperatures to about 1700°F (920°C). The alloy also has good resistance to.. |
|||
Tensile Strength, Yield | >= 725 MPa @Strain 0.200 % |
>= 105000 psi @Strain 0.200 % |
|
Schmolz + Bickenbach UGICHROM 4542 Martensitic Chrome Plated Bar Description: Ugichrom combines the high efficiency of micro-fissuring chromium plating with the technology of Ugitech’s most advanced gradesAdvantages: Zero defects guarantee; Low friction coef.. |
|||
Tensile Strength, Yield | 725 MPa @Strain 0.200 % |
105000 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum AL 418™ Special (Greek Ascoloy) Martensitic Stainless Steel Uses include engine braces, turbine exhaust components, exhaust struts, stiffeners, and ducts.Information provided by Allegheny Ludlum |
|||
Tensile Strength, Yield | <= 725 MPa @Strain 0.200 % |
<= 105000 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Altemp® 718 Nickel-Base Superalloy, Solution Treated Plate, UNS N07718 Allegheny Ludlum Altemp 718 alloy is an austenitic nickel-base superalloy which is used in applications requiring high strength to approximately 760 degrees Celsius and oxidation resistance to appro.. |
|||
Tensile Strength, Yield | 725 MPa @Strain 0.200 %, Temperature 95.0 °C |
105000 psi @Strain 0.200 %, Temperature 203 °F |
|
Haynes 242® alloy, hot rolled plate, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal.. |
|||
Tensile Strength, Yield | 725 MPa @Strain 0.200 % |
105000 psi @Strain 0.200 % |
|
Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |