Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 660 MPa @Strain 0.200 %, Temperature 760 °C |
95700 psi @Strain 0.200 %, Temperature 1400 °F |
|
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 660 MPa @Strain 0.200 % |
95700 psi @Strain 0.200 % |
|
Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | >= 660 MPa @Strain 0.200 % |
>= 95700 psi @Strain 0.200 % |
|
CLAL-MSX DECLAFOR® 1015 TDX Wire quenched/Cold Rolled Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn.. |
|||
Tensile Strength, Yield | 660 MPa | 95700 psi | |
Ametek 17-4 P/M Process, Sintered at 2300°F (1260°C) Composition reported is typical of 17-4 precipitation hardening stainless. This alloy is widely used because of its high strength, high hardness, excellent corrosion resistance, and easy heat treat.. |
|||
Tensile Strength, Yield | 660 - 830 MPa | 95700 - 120000 psi | |
ArcelorMittal Dual Phase 980 LCE Y660 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |