Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 35.2 MPa | 5110 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ HTX Ultra LA426 Gray 2382 Polyvinyl Chloride Alloy (PVC Alloy) Optimum for Black and Darker Colors between 50 and 70 L value. Also suitable for colors above 70 L value.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical propert.. |
|||
Tensile Strength, Yield | 35.2 MPa @Thickness 3.20 mm |
5100 psi @Thickness 0.126 in |
At 51mm/min, thick injection molded ASTM Type 1 specimen; ASTM D638 |
Pinnacle Polymers 1508 Polypropylene Homopolymer, Fiber Spinning Grade This Pinnacle Polymers Polypropylene is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties an.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | 2 in/min; ASTM D638 |
Phillips 66 COPYLENE® CH005 Polypropylene, Homopolymer, Extrusion, Strapping COPYLENE® CH005 is a fractional melt flow polypropylene homopolymer resin available in pellet form.Information provided by Phillips 66. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | (2 in/min); ASTM D638 |
Phillips 66 COPYLENE® CH350 Polypropylene Homopolymer COPYLENE™ CH350 is a controlled rheology, barefoot homopolymer designed for application as a base resin for compounding, consumer products and other injection molding applications.Applications: Inj.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D 638 |
LyondellBasell Moplen HP400L Polypropylene Homopolymer Description: All ingredients in HP400L meet the chemical registration requirements of TSCA (U.S.) and DSL (Canada). Uses: Toys, containers, lids, medical applications, closure capsInformation provid.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D 638 |
LyondellBasell Moplen HP400N Polypropylene Homopolymer Description: HP400N is a high flow homopolymer with a conventional molecular weight distribution and is formulated with a general-purpose additive package. HP400N is designed for injection molding a.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D 638 |
LyondellBasell Moplen HP550J Polypropylene Homopolymer Description: HP550J, a general purpose polypropylene homopolymer resin, is suitable for general extrusion and film fiber applications. HP550J resin meets FDA requirements in the Code of Federal Reg.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | 2 in/min; ASTM D638 |
M. Holland Company PP500 Polypropylene Homopolymer Features: Homopolymer, Narrow Molecular Wt. Dist.Uses: Disposable Drinkware, Medical Applications, PackagingApprovals: FDA 21 CFR 177.1520Processing Method: Injection MoldingInformation provided by .. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
Global ABS-704 General Purpose High Impact ABS Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Yield | 35.2 MPa @Temperature 23.0 °C |
5100 psi @Temperature 73.4 °F |
ASTM D638 |
Ineos H02G-02 Polypropylene Homopolymer This is a homopolymer designed for extrusion and film. It exhibits good extrusion and film orientation behavior. This material meets the requirements of the U.S. Food and Drug Administration as sp.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
Greene Tweed AR™ HT Abrasive-Resistant Thermoplastic ARHT™ is a proprietary thermoplastic material specifically developed for use a sbushings, bearings and wear rings in pumps handling abrasive media up to 250°F (121°C). ARHT provides outs.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
Spartech DP5120 Talc Filled Homopolymer Provides the highest level of stiffness and heat resistance of filled olefins. Talc filled grades offer the highest strength properties. Typical applications include extrusion/thermoformed food cont.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
Techmer ES Plastiblend® ABS 7000 Availability: North AmericaForms: PelletsFeatures: Low GlossInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS VP-12 Description: Flame Retardant with UVInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ASA S190 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ASA S519 Description: ASA Weatherable Polymer, Injection Molding Grade, Medium ImpactInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ASA S910 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | molded and tested in accordance with ASTM D 4101; ASTM D638 |
Dow H110-02N Polypropylene Resin DOW H110-02N is intended for use in extrusion and thermoforming processes. It is especially suited for applications where improved melt strength and clarity are desired.Information provided by DowD.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5110 psi | ASTM D638 |
Dow NRD6-589 Polypropylene Random Copolymer Resin DOW NRD6-589 Polypropylene Resin is intended for use in injection molding applications. It offers excellent balance of impact and stiffness.Consistent processabilityGood stiffness/impact balanceGoo.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5110 psi | ASTM Data |
Dow Prevail® 3050 ABS + Polyurethane PREVAIL® 3050 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
Tensile Strength, Yield | 35.2 MPa | 5110 psi | 2 in/min (50 mm/min); ASTM D638 |
Bapolene® 4071 Polypropylene, Fiber/Injection Grade Bapolene PP4071 is a high flow PP homopolymer for staple and continuous filament applications as well as general purpose injection molding. This resin exhibits good melt and thermal stability.Appli.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
Amco Amalloy® B1172 Polymer Alloy Amco Amalloy B1172 is a proprietary copolymer with exceptional clarity and enhanced impact strength.Impact modified, very clear, moderate flow.Information provided by Amco Plastic Materials. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
Amco PRIMATOP HDPE RP 011 Granular High Density Polyethylene HDPE RP 011 features small particle size and is used in plastic lumber extrusion.Former A-Top Polymers product; part of Amco product line since 2013. |
|||
Tensile Strength, Yield | 35.2 MPa | 5110 psi | ASTM D412 |
ACC EP RAP 60 EPI Engineered Polymers Aliphatic Polyurea EP RAP 60 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, coating (silicone optional) developed for UV stable (colorfast) polyurea flooring applic.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
Aaron Industries AAROLENE® ARPP H 200-1 PP Black Polypropylene Homopolymer Compounded Resin AAROLENE® ARPP 200 Series Polypropylene Compounded ResinFeatures: A pre-colored, black homopolymer polypropylene resin specifically designed for all injection molding applications.High Flow |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | 2" (50mm) per min; ASTM D638 |
Formosa Plastics Formolene® 5181K Homopolymer Polypropylene Homopolymer for Extrusion Applications Including Straws Formolene® 5181K is a high molecular weight, highly isotactic, polypropylene homopolymer containing anti-stat designed for straws and cutlery.. |
|||
Tensile Strength, Yield | 35.2 MPa @Temperature 23.0 °C |
5100 psi @Temperature 73.4 °F |
ASTM D638 |
Ineos H12G-00 Polypropylene Homopolymer This is a general purpose homopolymer for injection molding applications. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsG.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5110 psi | ASTM D638 |
Dow H110-02NZ Polypropylene Homopolymer Resin OverviewContains a nucleating agentGood melt strengthComplies with U.S. FDA 21 CFR 177.1520 (c)3.2aDOW H110-02NZ Polypropylene Resin is intended for use in extrusion and thermoforming processes in o.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5110 psi | ASTM D638 |
Braskem INSPIRE™ 222 Performance Polypropylene Polymer INSPIRE™ 222 Performance Polymer is intended for use in extrusion and thermoforming processes. It is especially suited in applications requiring excellent clarity and good stiffness.Contains a nuc.. |
|||
Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
Techmer ES HiFill® PA12 1100 Tungsten Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Tungsten FillerInformation provided by TP Composites, Inc. |