Polymer Property : Film Tensile Strength at Break, MD = 145 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	145 MPa	21000 psi	ExxonMobil Method
ExxonMobil Bicor® 100 CSR-2 OPP Film Product Description: Bicor CSR-2 is a one-side treated OPP film designed for cold seal release, either unsupported or as the outer web of a lamination.Availability: Latin America, North America and ..
Film Tensile Strength at Break, MD	145 MPa	21000 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 25ICT OPP Film Product Description: A one-side sealable, very broad seal range coextruded BOPP. This film is designed for use in unsupported plain or surface printed high-speed horizontal applications. The enhance..
Film Tensile Strength at Break, MD	145 MPa	21000 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 30MM680 OPP Film Product Description: A biaxially oriented polypropylene film, metalized on one side, heat sealable on the other side. Typically, all gauges are used laminated with other substrates on HFFS and VFFS ..
Film Tensile Strength at Break, MD	145 MPa	21000 psi	ASTM D882A
DuPont Teijin Films Mylar® WRL63 Polyester Film, 200 Gauge Mylar® WRL63 is a biaxially oriented polyester (OPET) film with a modified ethylene acrylate heat seal layer. It provides peelable seal over a broad temperature range to a number of bottles or cont..