ExxonMobil Bicor™ 25ICT OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Bicor™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Bicor™ 25ICT OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A one-side sealable, very broad seal range coextruded BOPP. This film is designed for use in unsupported plain or surface printed high-speed horizontal applications. The enhanced print layer, suitable for use with coex or coated ink systems, offers constant and consistent slip properties.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Superior printing efficiency on the printable layerConsistent and stable slipExcellent hot slipVery broad sealing rangeExcellent hot tackExcellent optical propertiesFeatures:Very Broad Seal RangeApplications:BakeryBiscuits/Cookie/CrackersConfectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksFresh ProduceFrozen FoodHealth and Beauty CareHousehold and DetergentsIce CreamPet Food Uses: HFFS Flexible Packaging Processing Method: Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 1.10 g/m²/day

@Temperature 23.0 °C
0.0710 g/100 in²/day

@Temperature 73.4 °F
85% RH; ExxonMobil Method
4.97 g/m²/day

@Temperature 38.0 °C
0.320 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Thickness 24.9 microns
0.980 mil
ExxonMobil Method
Coating Weight 21.8 g/m²
13.6 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 175 %
175 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 65 %
65 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 2.00 GPa
290 ksi
MD; ExxonMobil Method
3.80 GPa
551 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.28
0.28
Treated; ExxonMobil Method
0.40
0.40
Untreated; ExxonMobil Method
Seal Strength 410 g/25 mm

@Pressure 0.138 MPa
410 g/in

@Pressure 20.0 psi
ESM, 0.8 sec, Untreated; ExxonMobl Method
Film Tensile Strength at Break, MD 145 MPa
21000 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 270 MPa
39200 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 6.0 %

@Temperature 135 °C,
Time 432 sec
6.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Haze 1.3 %
1.3 %
ExxonMobil Method
Gloss 85 %
85 %
45°; ExxonMobil Method
Descriptive Properties Value Comments
Heat Seal Range 99°F
36.3 psi, 0.2 sec
Yield 31600 in2/lb