Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 405 MPa @Strain 1.00 % |
58700 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
Outokumpu 4742 High Temperature Ferritic Stainless Steel Good scaling resistance and can be subjected to reducing sulphur environments without risk. Subject to 475°C embrittlement and grain coarsening at temperatures above 950°C. s-phase may form afte.. |
|||
Tensile Strength, Yield | 405 MPa @Strain 0.200 % |
58700 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
Outokumpu 4762 High Temperature Ferritic Stainless Steel Highest chromium content-most resistant to reducing sulphurous gases. Susceptible to 475°C embrittlement and s-phase forms during long exposures in the range 600-800°C.Applications: Mostly used i.. |
|||
Tensile Strength, Yield | >= 405 MPa @Temperature 20.0 °C |
>= 58700 psi @Temperature 68.0 °F |
|
PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6x Heat Treatment Condition T6x (Quench in water at RT). Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials all.. |
|||
Tensile Strength, Yield | 405 MPa @Thickness 12.7 mm, Temperature 204 °C |
58700 psi @Thickness 0.500 in, Temperature 399 °F |
0.2% Offset |
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
Tensile Strength, Yield | 405 MPa @Thickness 3.20 mm, Temperature 25.0 °C |
58700 psi @Thickness 0.126 in, Temperature 77.0 °F |
0.2% Offset |
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
Tensile Strength, Yield | 405 MPa @Diameter 12.7 mm, Temperature 427 °C |
58700 psi @Diameter 0.500 in, Temperature 801 °F |
0.2% Offset |
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
Tensile Strength, Yield | >= 405 MPa @Strain 0.200 %, Thickness 120 - 140 mm |
>= 58700 psi @Strain 0.200 %, Thickness 4.72 - 5.51 in |
|
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m.. |
|||
Tensile Strength, Yield | 405 MPa @Thickness 12.7 mm, Temperature 371 °C |
58700 psi @Thickness 0.500 in, Temperature 700 °F |
0.2% Offset |
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe.. |