Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 724 MPa @Strain 0.200 % |
>= 105000 psi @Strain 0.200 % |
H1150 Condition - 620°C at 4 hr |
Latrobe Lescalloy® 17-4 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150°F (482-621°C) tempe.. |
|||
Tensile Strength, Yield | 724 MPa @Strain 0.200 % |
105000 psi @Strain 0.200 % |
5.25 in. Test Specimen |
Latrobe Lescalloy® 410Cb High Strength Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150°F (482-621°C) tempe.. |
|||
Tensile Strength, Yield | 727 MPa @Strain 0.200 %, Diameter 12.7 mm |
105000 psi @Strain 0.200 %, Diameter 0.500 in |
As Welded and Aged at 1850°F(1010°C)/2hr/AC + 1450°F(788°C)/8h/AC |
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Tensile Strength, Yield | 724 MPa @Strain 0.200 %, Thickness <=38.1 mm |
105000 psi @Strain 0.200 %, Thickness <=1.50 in |
Tension |
Crucible Steel Aquamet® 19 Stainless Steel AQUAMET 19 is a modified Type 304 stainless steel that is fully austenitic and non-magnetic. Strengthened by adding nitrogen to the melt, it has better corrosion resistance than Type 304 stainless. .. |
|||
Tensile Strength, Yield | 721 MPa @Strain 0.200 % |
105000 psi @Strain 0.200 % |
50% Cold Worked |
AK Steel 409 ULTRA FORM® Stainless Steel AK Steel 409 ULTRA FORM Stainless Steel provides an outstanding combination of improved forming and welding characteristics, while providing superior resistance to oxidation, corrosion, ridging and .. |
|||
Tensile Strength, Yield | >= 724 MPa @Strain 0.200 % |
>= 105000 psi @Strain 0.200 % |
AMS 5542 aged, sheet |
ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information.. |
|||
Tensile Strength, Yield | >= 724 MPa @Strain 0.200 % |
>= 105000 psi @Strain 0.200 % |
AMS 5598 aged, plate |
ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information.. |