Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 82.0 MPa @Temperature 23.0 °C |
11900 psi @Temperature 73.4 °F |
DAM; ISO 527 |
DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66
(Unverified Data**) Minlon® 10B140 BK061 is a 40% mineral reinforced, black polyamide 66 resin for injection molding. It has very low warpage.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 82.0 MPa @Temperature 175 °C |
11900 psi @Temperature 347 °F |
4; ISO 527-2 |
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Dry) Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high stre.. |
|||
Tensile Strength at Break | 82.0 MPa @Temperature 100 °C |
11900 psi @Temperature 212 °F |
DAM; ISO 527 |
DuPont Performance Polymers Zytel® 84G33 BKB031 Nylon 66
(Unverified Data**) Zytel® 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was developed for applications requiring strength, stiffness and im.. |
|||
Tensile Strength at Break | 82.0 MPa @Temperature 175 °C |
11900 psi @Temperature 347 °F |
ISO 527-2 |
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA)
(Unverified Data**) Amodel A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength.. |